Abstract:The widespread use of sodium aluminosilicate glass in many engineering applications due to its mechanical and optical properties (transparency, dielectric, etc.), has become common in recent years. However, glass, a brittle material, has its vulnerability to fracture. Processes such as heat treatment (heat tempering) or chemical strengthening through ion-exchange have been used to create residual stress profiles on the glass, in a bid to improve its fracture strength. However, failure still occurs, which is mostly catastrophic and expensive to repair. Therefore understanding, predicting, and eventually improving the resistance to damage or fracture of chemically strengthened glass is important to designing new glasses that would be tougher while retaining their transparency. The relationship between the glass residual stress parameters such as the compressive stress (CS), depth of compression layer (DOL), and central tension (CT) versus apparent (effective) fracture toughness for different crack depth was investigated in this study using a Silicon Carbide particle blast plus ring-on-ring (RoR) test method. The results also showed that improving the fracture resistance of glass via chemical strengthening requires a proper combination of CS, DOL, and CT, which is particularly dependent on the initial/existing crack (flaw) depth. It was determined that for a damage event involving the introduction of a shallow crack depth, the criterion for optimal resistance to fracture, in terms of apparent fracture toughness, is weighted more towards a high CS, than deep DOL while for a deep flaw damage event, it is more weighted towards deep DOL, than a high CS. These results provide a valuable piece of information in the design of a more robust glass in engineering applications.

Experimental investigation on thermal healing of subsurface damage in borosilicate glass

Effect of Temperature on Surface Error and Laser Damage Threshold for Self-Healing BK7 Glass

Numerical Simulation and Experimental Study on Crack Self-Healing in BK7 Glass

Kinetic model and effect of surface impurities on the crack healing of BK7 glass

Subsurface damage evaluation in the single abrasive scratching of BK7 glass by considering coupling effect of strain rate and temperature

Investigation on the smoothing of surface spatial frequency errors for borosilicate glass by heat-treatment

A Method to Study the Crack Healing Process of Glassformers

Experimental Investigation of Enhancing the Subsurface Damage Threshold of Nd-Doped Phosphate Glass

Relationship Between Subsurface Damage and Surface Roughness of Glass BK7 in Rotary Ultrasonic Machining and Conventional Grinding Processes

EXPERIMENTAL INVESTIGATIONS ON SUBSURFACE DAMAGE IN ROTARY ULTRASONIC MACHINING OF GLASSBK7

Assessment of sub-micron subsurface damage in glass

Investigation on the influence of the CO2 laser parameters on the defect healing process of fused silica

The Competing Effect of Initial Crack Depth Versus Chemical Strengthening Parameters on Apparent Fracture Toughness of Sodium Aluminosilicate Glass

Experimental Investigation on Laser-Induced Surface Damage Threshold of Nd-Doped Phosphate Glass

Scratch-induced micro-fracture behaviour and translational failure of glass: An experimental and numerical study

Crack arrest and stress dependence of laser-induced surface damage in fused-silica and borosilicate glass

Experiment of Laser Induced Damage Threshold for Different Sub-Surface Cracks on Fused Silica

Theoretical and experimental investigation on surface generation and subsurface damage in fixed abrasive lapping of optical glass

Relationship Between Surface Roughness and Subsurface Crack Depth During Grinding of Optical Glass BK7

Simulation Study On The Influence Of Subsurface Deficiency On Fused Silica Laser Damage Threshold

Delayed fracture of ion‐exchange strengthened alkali‐aluminosilicate glass