Abstract:Cerium-tungsten oxides could reconfigure the redox sites and acid sites of red mud based catalyst.Cerium-tungsten supported red mud based catalyst kept above 90% NOx conversion at 219 – 480 °C.Abundant Ce3+ and unsaturated chemical bond improved the redox properties of catalyst.Ce2(WO4)3 formed by solid-state reaction between Ce and W species promoted NH3 adsorption.Activated red mud (RM) has been proved to be a promising base material for the selective catalysis reduction (SCR) of NOx. The inherent low reducibility and acidity limited its low-temperature activity. In this work, molybdenum oxide, tungsten oxide, and cerium oxide were used to reconfigure the redox sites and acid sites of red mud based catalyst. When activated red mud was reconfigured by cerium-tungsten oxide (), the NOx conversion kept above 90% at 219 – 480 °C. The existence of Ce3+/Ce4+ redox electron pairs provided more surface adsorbed oxygen (Oα) and served as a redox cycle. Positive interactions between Ce, W species and Fe oxide in red mud occurred, which led to the formation of unsaturated chemical bond and promoted the activation of adsorbed NH3 species. WO3 and Ce2(WO4)3 (formed by solid-state reaction between Ce and W species) could provide more Brønsted acid sites (W-O modes of WO3, W=O or W-O-W modes of Ce2(WO4)3). CeO2 species could provide more Lewis acid sites. The Langmuir-Hinshelwood (L-H) routes and Eley-Rideal (E-R) routes occurred in the low-temperature SCR reaction on the surface. NH4+ species on Brønsted acid sites, NH3 species on Lewis acid sites, bidentate nitrate and bridging nitrate species were key active intermediates species.<ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S246802572100056X-ga1_lrg.jpg">Download : Download high-res image (226KB)</a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S246802572100056X-ga1.jpg">Download : Download full-size image</a></li></ol>

Getting insight into the effect of CuO on red mud for the selective catalytic reduction of NO by NH3

Investigation on the redox/acidic features of bimetallic MOF-derived CeMOx catalysts for low-temperature NH3-SCR of NOx

Insights into the Effects of Sulfate Species on CuO/TiO2 Catalysts for NH3-SCR Reactions

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Insights into the active sites of copper species in CuO/SiO 2 catalysts for NH 3 -SCR: Quantitative analysis and mechanism study

Insights into the active sites of copper species in CuO/SiO2 catalysts for NH3-SCR: Quantitative analysis and mechanism study

Cerium-tungsten oxides supported on activated red mud for the selective catalytic reduction of NO

Modified red mud catalyst for the selective catalytic reduction of nitrogen oxides: Impact mechanism of cerium precursors on surface physicochemical properties

Bimetallic Cerium–copper Nanoparticles Embedded in Ordered Mesoporous Carbons As Effective Catalysts for the Selective Catalytic Reduction of NO with NH3

Effect of Cu loading content on the catalytic performance of Cu-USY catalysts for selective catalytic reduction of NO with NH3

Cu-ZSM-5 Catalyst Impregnated with Mn–Co Oxide for the Selected Catalytic Reduction of NO: Physicochemical Property–Catalytic Activity Relationship and In Situ DRIFTS Study for the Reaction Mechanism

Promotional Synergistic Effect of Cu and Nb Doping on a Novel Cu/Ti-Nb Ternary Oxide Catalyst for the Selective Catalytic Reduction of NOx with NH3

Selective Catalytic Reduction of NO over Cu-Mn/OMC Catalysts: Effect of Preparation Method

CuOx and WOx modified CeO2-TiO2 with various morphologies for the selective catalytic reduction of NOx with NH3

The Selective Catalytic Reduction Activity of Cu/MCM-41 Catalysts Prepared by Using the Cu2+–MCM-41 Mesoporous Materials with Copper Ions in the Framework As Precursors

Effect of Cu loading on the performance and kinetics of Cu/SAPO-34 catalysts for selective catalytic reduction with NH3

Controlled synthesis of Cu-based SAPO-18/34 intergrowth zeolites for selective catalytic reduction of NOx by ammonia

In situ regeneration of sulfated Cu/SAPO-34 catalyst for the selective catalytic reduction of NOx with NH3

High-performance Fe-Cu composite oxide for selective catalytic reduction of NO with NH3: Driving of Cu on α-Fe2O3

Structure, Acidity and Activity of CuOx/WOx–ZrO2 Catalyst for Selective Catalytic Reduction of NO by NH3

Effective reduction of nitric oxide over a core–shell Cu-SAPO-34@Fe-MOR zeolite catalyst