Abstract:The main objective of this research was to investigate the effect of adding CuO (2 wt.%) nanoparticles and changing the cooling rate on the microstructure and mechanical properties of Al (2 wt.%) Si. The addition of CuO nanoparticles to Al-2wt.%Si (alloy A) resulted in a composite alloy (alloy B). Optical microscopy (OM), scanning electron microscopy (SEM) connected to an energy-dispersive spectrometer (EDS), x-ray diffraction (XRD), and positron annihilation Doppler broadening spectroscopy (PADBS) were used to examine the microstructure of alloys. Moreover, Vickers hardness and tensile tests were used to investigate the mechanical properties of the tested alloys. The G1 samples were cooled in the air to ~ 300 K and quenched G2 samples in cold water at 0 °C. The results showed that increasing the strain rate from 0.004 to 0.02 min −1 or decreasing the temperature from 503 to 423 K could increase the hardening parameters, yield stress ( σ y ), ultimate strength ( σ M ), and Young's modulus ( Y ) of all samples. Moreover, H V decreased as the aging temperature climbed from 423 to 503 K. Adding nano-sized CuO or cooling samples resulted in smaller grains. Furthermore, alloy B exhibited the formation of intermetallic compounds (IMCs) CuAl 2 and Cu 3 Si. The XRD data indicated the formation of phases in both alloys at 423, 463, and 503 K. In addition, the dislocation density, lattice strain, and average crystallite size were calculated. It can be seen from the activation energies and stress exponents that dislocation climbs through core diffusion as a control mechanism for both alloys. A significant positive relationship was observed between the value ( H v ) and PADBS parameters for all examined samples. The investigation showed that nano-sized CuO and a rapid cooling rate increased composite specimen hardness. This finding confirms that aluminum and its alloys play a crucial role in various technical applications.

A Comparative Study on Microstructure, Mechanical Property and Damping Capacity of Hypoeutectic Al–Si–Cu Alloy for Different Casting Technologies

Microstructure and damping properties of Mg–Si binary hypoeutectic alloys

The effect of squeeze casting process on the microstructure, mechanical properties and wear properties of hypereutectic Al–Si–Cu–Mg alloy

Comparison of the semisolid squeeze casting and gravity casting process on the precipitation behavior and mechanical properties of the Al-Si-Cu-Mg alloy

Microstructural refinement and tensile properties enhancement of Al-10Mg2Si cast alloys by copper addition

Effect of CuO Nanostructure Addition and Cooling Rate on the Microstructure and Mechanical Characteristics of Hypoeutectic Al-2wt.%Si Alloy

Effect of Casting Process and Thermal Exposure on Microstructure and Mechanical Properties of Al-Si-Cu-Ni Alloy

A Comparative Study on Microstructure, Mechanical Property, and Electrical Conductivity of Al-7Si-0.6Mg Alloy Produced by High Pressure Die Casting and Semisolid Die Casting

Microstructure and high temperature tensile properties of Al–Si–Cu–Mn–Fe alloys prepared by semi-solid thixoforming

Study on the Effect of Pre-Refinement and Heat Treatment on the Microstructure and Properties of Hypoeutectic Al-Si-Mg Alloy

Formation of Spheroidal Microstructure in Semi-solid State of Al-4.8Si-2.8Cu-0.5Mg Aluminium Alloy

Effect of Cooling Rate on the Microstructure and Mechanical Properties of Al-5Cu-0.38Mg-0.32Mn-0.1Ag Alloy Cylinder Heads

Enhanced comprehensive performance via alloying and rheo-diecasting in a semi-solid Al–Si–Fe–Mg–Cu–Sr alloy

The effect of Cu–8%P master alloy, SIMA process, thixoforming, and heat treatment on the microstructure and mechanical properties of Al–20%Mg 2 Si composite

Optimizing the Pouring Temperature for Semisolid Casting of a Hypereutectic Al–Si Alloy Using the Cooling Slope Plate Method

Effect of ageing and thermal exposure on microstructure and mechanical properties of a HPDC Al–Si–Cu–Mg alloy

Influence of Rheo-Diecasting Processing Parameters on Microstructure and Mechanical Properties of Hypereutectic Al–30%Si Alloy

Microstructure and Tribological Property Correlations of Die Cast and Spray Formed Al-30 wt.% Si Alloy

Comparative analysis on high temperature tribological behaviour of additive manufactured and cast AlSi10Mg alloy

Effect of chemical composition and T6 heat treatment on microstructure and mechanical properties of a hyper eutectic Al–Si alloy

Microstructural evolution and mechanical property of Al–Mg–Mn alloys with various solidification cooling rates