Abstract:The currently used low carbon operation in blast furnaces (BFs) leads to a thin coke layer and deterioration in gas and liquid permeability. Previous studies have reported that coke breeze, formed by the graphitization of coke, is one of the main influences on gas and liquid permeability in the high-temperature zone of a BF. To investigate the influence of the graphitization of BF coke on its metallurgical properties, the degree of coke graphitization under different heating temperatures from 1100 to 1500℃ was investigated. The dependence of the degree of graphitization on coke reactivity index (CRI) and coke strength after reaction (CSR) was also studied. The relationship between different degrees of graphitization in coke and alkali metals was clarified. Finally, the micro-morphology of coke was inspected and analyzed. Results show that with increasing temperature, the degree of coke graphitization intensifies. With every 100℃ rise in heating temperature, the degree of coke graphitization increases 1.8 times, the value of the spacing of layers (d002) decreases by 2%, and the values of the layers diameter of microcrystalline structure (La) and the stack height (Lc) are improved by 3% and 15%, respectively. In addition, it is observed that the surface stomata of the coke decreases particularly the large pores, the mosaic structure decreases, the isotropic structure increases, and the degree of structural ordering increases. When the degree of graphitization intensifies, the CRI of the coke gradually decreases, the CSR gradually increases, the degree of coke degradation weakens, the formed large pores reduced, and the trend for pore wall damage is reduced. Moreover, the alkali metal plays a catalytic role in improving the CRI and decreasing the CSR. It is considered that the graphitized coke resists the destruction of the alkali metal and thus decreases the degree of coke degradation.

Study of the microstructure of special types of coke from Kazakhstan

Evolution of Coke Microstructure and Metallurgical Properties During Graphitization in a Blast Furnace

Research on themetallurgical properties of coke used in Tangsteel ironmaking production

Pore Structure Evolution During the Coke Graphitization Process in a Blast Furnace

Influence of Sodium on Coke Microstructure in Different Reaction Atmosphere

Analysis and Study on Needle Coke of Microstructure with Optical Microscope

Influence of the Heating Rate on the Quality of Metallurgical Coke

Effect of blast furnace coke graphitizing its high temperature metallurgical properties

A Comprehensive Review of Characterization Methods for Metallurgical Coke Structures

In-situ study of the heating rate effects on covalent bonds conversion and pore/carbon microcrystal evolutions of coal molecule during coking

Study on Relationships between Coal Microstructure and Coke Quality during Coking Process

Study progress of characterization methods for coke structure

Isothermal and non-isothermal CO2 gasification kinetics of charging coke and raceway coke used in a blast furnace

Microstructure Evolution Behavior of Blast-Furnace Coke under Different Gasification Reaction Conditions

Mathematical Model of Optimum Control for Petroleum Coke Production in a Rotary Tube Kiln

Highly Reactive Coke Made from Low-rank Coal: Relationship Between Thermal Properties and Multilevel Structure

Effect of gasification reaction on pore structure, microstructure, and macroscopic properties of blast furnace coke

OBTAINING POROUS CARBON MATERIAL AND INVESTIGATION OF ITS PHYSICAL AND CHEMICAL PROPERTIES

Generation and characterization of coal-based needle coke produced by the co-carbonization of coal liquefaction pitch and anthracene oil

Synthesis of needle coke by co-carbonization of coal liquefaction pitch and refined soft pitch

Mechanism of carbon structure transformation in plastic layer and semi-coke during coking of Australian metallurgical coals