Abstract:Soft coal tar pitch (SCTP) with low QI content is the preferred raw material for preparing coal-based needle coke, the study on its structure changes in the stage of liquid-phase carbonization into coke (350 similar to 550 degrees C) is helpful to prepare high-quality needle coke. In this paper, a detailed analysis on the C-H stretching vibration peaks in the range of 3 100 similar to 2 800 cm(-1) and the aromatic C-H bending vibration peaks in the range of 900 similar to 700 cm(-1) has been carried by the peak-fitting technique using the infrared spectra of the sample. And then based on the calibration factors of the corresponding C-H vibration peaks for the stand- ard substances, the mass percentages of the different types of aromatic hydrogen (H-solo , H-duo, H-trio and H-quarto) and aliphatic hydrogen (H-CH3, H-CH2 and H-CH) of SCTP were quantitated at different carbonization temperatures (400, 500, 600 and 800 degrees C). Furthermore, the contents of SP2 hybridized Carbon ((SPC)-C-2) and SP3 hybridized Carbon ((SPC)-C-3) as well as these structural parameters such as H/C atomic ratio, aromatic index (I-ar) , aromatic ortho-substitution index (I-os) and branched index (CH3/CH2) were calculated, and the changes of aromatic structure of SCTP during the coking process were also discussed. The results showed that the coal-based needle coke raw material SCTP is mainly composed of aromatic hydrocarbons with a low number of the ring and few side chains, its I(ar )is 0. 77, and about 82% of its aromatic hydrogen is distributed in the structure containing three/four adjacent aromatic C-H, while its aliphatic hydrogens are mainly distributed in the CH2 of naphthenic structures. With the increase of carbonization temperature, the aliphatic hydrogen or (SPC)-C-3 of SCTP decreased almost linearly, losing about 50% at 400 degrees C , which was mainly attributed to the loss of light components and the dehydrogenation of naphthenic structures. The green coke formed at 500 degrees C had Only 0. 15 Wt. % aliphatic hydrogen and 0. 88 Wt. % SP3 C, and the presence of aliphatic hydrogen was not detected at 600 degrees C. However, the aromatic hydrogen increased slightly from 3. 89 Wt. % of the raw material to 4. 5 Wt. % before 400 degrees C because of the conversion of the naphthenic structuresinto aromatic rings. As the temperature increases further, aromatic hydrogen decreases rapidly, reaching only 1. 14 Wt. % when the temperature reaches 500 degrees C , indicating that the aromatic hydrocarbon molecules undergo intense dehydrogenation condensation reaction during the mesophase formation stage at 400 similar to 500 degrees C , which was also confirmed by the conversion of a large number of protonated (SPC)-C-2 into unprotonated (SPC)-C-2. Aromatic hydrogen continued to decrease after 500 degrees C , and their presence was not detected at 800 degrees C. In addition, it was found that the out-of-planebending vibration of aromatic C-H is more sensitive to infrared light than its in-plane stretching vibration. The increase of I-ar and the decrease of these parameters such as H/C atomic ratio, I-os, CH3/CH2, indicated that the aromatic molecules in the SCTP are gradually grown up by their condensation, and its aromaticity increased in the coking process. The fast quantification of various types of hydrogen by infrared spectrum can timely understand the structural changes of aromatic hydrocarbon molecules of the pitch in the coking process, which is helpful to the production of needle coke.

Synthesis of needle coke by co-carbonization of coal liquefaction pitch and refined soft pitch

Generation and characterization of coal-based needle coke produced by the co-carbonization of coal liquefaction pitch and anthracene oil

Effects of co-carbonization of medium and low temperature refined pitch and high temperature refined pitch on the structure and properties of needle coke

Preparation and Characterization of Coal Pitch-Based Needle Coke (Part II): The Effects of β Resin in Refined Coal Pitch

Preparation and Characterization of Coal-Pitch-Based Needle Coke (Part III): The Effects of Quinoline Insoluble in Coal Tar Pitch

Characteristics of the mesophase and needle coke derived from the blended coal tar and biomass tar pitch

Co-carbonization behavior of the blended heavy oil and low temperature coal tar for the preparation of needle coke

Co‐Carbonization of Medium‐ and Low‐Temperature Coal Tar Pitch and Coal‐Based Hydrogenated Diesel Oil Prepare Mesophase Pitch for Needle Coke Precursor

Effect of adding graphene oxide on the structure and properties of needle coke

Synthesis and characterization of mesophase coke from medium–low‐temperature coal tar pitch modified by high‐pressure thermal polymerization

Preparation and characterization of mosaic coke from heavy‐phase coal pitch

REDUCTION OF PUFFING BY NITROGEN COMPOUNDS IN COAL-BASED NEEDLE COKE PRECURSORS FOR ELECTRODE GRAPHITE

Preparation and characterization of pitch coke from oxidized polymerized pitch

Differences and correlations between microstructure and macroscopic properties of mesophase cokes derived from the components of high temperature coal tar pitch

Spinnable Mesophase Pitch Prepared via Co-carbonization of Fluid Catalytic Cracking Decant Oil and Synthetic Naphthalene Pitch

Infrared Spectroscopic Quantitative Analysis of Raw Material Used As Coal-Based Needle Coke in the Coking Process

The effect of n-heptane soluble content on the composition and structure of coal tar pitch and the preparation of needle coke

Changes in structure of coal liquefied pitch during liquid-phase carbonization process

Tailoring the Optical Properties of Coal Pitch-Derived Carbon Dots by Graphitization Controlling