Abstract:The use of highly specialized alloys in ethane steam cracking environments can lead to reduced coking and alloy aging. However, the fouling resistance of these materials when exposed to heavier feedstocks, such as butane, especially at higher temperatures (950 °C) and toward the end of a cracking run, remained unknown. To address this knowledge gap, this study investigated the coke resistances of presulfided three alloys, Al-Boosted, Spinel-Coated, and 35/45 Cr–Ni, during the steam cracking of both ethane and butane using a quartz Electrobalance setup with a tubular reactor. Under experimental conditions of T gas = 950 °C, P = 1.1 bar, χButane ≈ 79%, χEthane ≈ 68%, dilution δ = 0.4 kgH2O/kgHC, and DMDS = 48 ppmw S/HC, the results revealed that butane cracking exhibited higher coking compared to ethane for the Al-Boosted and 35/45 Cr–Ni. This difference was attributed to the generation of larger quantities of coke precursors, such as aromatics, naphthenes, and butadiene, during butane cracking. Notably, the Al-containing alloy displayed exceptional resistance to aging, in contrast to the non-Al-containing alloys, which experienced severe carburization and aging effects after multiple cracking cycles. Detailed scanning electron microscopy (SEM) and energy-dispersive X-ray (EDX) analyses indicated that the presence of a continuous and robust Al2O3 layer on the surface of the Al-containing alloy provided significant protection to the catalytic sites within the material. The average catalytic coking rate for the Al-containing alloy during butane cracking was measured at 5.83 × 10–6 kg m–2 s–1, while for the non-Al-containing alloys, it ranged from 7.26 × 10–6 to 15.25 × 10–6 kg m–2 s–1. Furthermore, this study explored the relative influence of the feedstock and reactor material, revealing that for the Al-Boosted alloy, the feedstock had a greater impact on coking behavior. Conversely, for the 35/45 Cr–Ni alloy, aging had a more pronounced effect compared to that of the specific feedstock used. This research provides valuable insights into the fouling behavior of specialized alloys in the steam cracking of ethane and butane. The study highlights the superior resistance to aging and reduced coking rate exhibited by the Al-containing alloy, underscoring the protective role of the Al2O3 layer. Additionally, it emphasizes the relative significance of both feedstock composition and reactor material on coking tendencies, thereby contributing to a better understanding of fouling mechanisms in the steam cracking process.

Influence of Sodium on Coke Microstructure in Different Reaction Atmosphere

Catalytic Effect of Alkali Metals on the Gasification Dissolution Reaction and Deep Reaction Behavior of Metallurgical Cokes.

Evolution of Coke Microstructure and Metallurgical Properties During Graphitization in a Blast Furnace

To stimulate, and to inhibit: A theoretical understanding of the sodium-catalytic mechanism of coke gasification

Catalytic effect and kinetic mechanism of alkali metal carbonates on the reduction reaction of biochar with iron oxide

Degradation Behaviors of Coke under Complex Solution Loss Conditions

Production of highly reactive cokes by adding alkali metals and alkaline earth metals and their effect mechanism

Impacts of Alkali or Alkaline Earth Metals Addition on Reaction Intermediates Formed in Methanation of CO2 over Cobalt Catalysts

Influence of Na2CO3 on combustion performance of civil clean coke

Mechanistic insight into catalytic effect of typical native impurities on coke oxidation and oxygen-gasification via in-situ detection, ReaxFF MD, and DFT

Difference in Radial Direction of Lumpy Coke Sampling from Raceway of Large Blast Furnaces: Microstructure, Alkali Enrichment, and Solution Loss Reaction

Influence of alkali metal K on the gasification reaction of ferro-coke with CO2

Influence of alkali metal Na on coal-based soot production

Effects of Microwave Modification on the Desulfurization and Denitrification of Activated Coke

Influence of the Heating Rate on the Quality of Metallurgical Coke

Effects of Microscopic Characteristics on Post-Reaction Strength of Coke

The solution-loss reaction of cokes with different reactivity and lump ores during reductive coupling

A comprehensive investigation on the structural transformation and dissolution loss reaction of coke during gasification in CO 2 atmosphere

Effect of Five Different Additives on the Sintering Behavior of Coal Ash Rich in Sodium under an Oxy-Fuel Combustion Atmosphere

Biomass and Coal Modification to Prepare Activated Coke for Desulfurization and Denitrification

Effect of Reactor Alloy Composition on Coke Formation during Butane and Ethane Steam Cracking