Effect of cold rolling on microstructure and texture evolution in strip casting Fe-36%Ni invar alloy foil

Hong-Yu Song,Guo-Dong Wang,Hai-Tao Liu

DOI: https://doi.org/10.1016/j.jallcom.2021.161519

IF: 6.2

2021-12-01

Journal of Alloys and Compounds

Abstract:A new processing route including strip casting, cold rolling and annealing was proposed to manufacture the 0.05 mm-thick Fe-36%Ni invar alloy foil. The as-cast strip had coarse columnar austenite grains and pronounced {100}<0vw>fiber texture due to the high melt superheat during strip casting. The severe cold rolling in one-stage cold rolling route led to inhomogeneous deformed microstructures and strong copper-type textures. The striking features were the absence of Cube texture ({001}<100>) in the 0.05 mm-thick cold rolled strip and the appearance of {001}<310>texture after annealing, differing from the results that sharp Cube texture was normally the unique annealing texture in case of severe cold rolling. By contrast, two-stage cold rolling route led to the sharp Cube texture after final annealing even the cold rolling reduction was as high as 92.9%. The different microstructures prior to final cold rolling may be responsible for the evolution of Cube and {001}<310>texture in various routes.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering