Microstructure and Texture Evolution of Al0.3CoCrFeNi High-Entropy Alloy After Cold Rolling Deformation

Amirhossein Hosseinifar,Kamran Dehghani

DOI: https://doi.org/10.1007/s12666-024-03271-6

2024-02-16

Transactions of the Indian Institute of Metals

Abstract:It has been tried in this research for investigating the microstructure and texture of Al 0.3 CoCrFeNi after the cold rolling process. At first, an ingot was made by vacuum arc melting. Then, homogenization heat treatment was done at 1050 °C for 10 h to eliminate casting defects. After that, cold rolling deformation with 75% reduction was applied, and the thickness of the ingot reached 2 mm from 8 mm. Finally, annealing heat treatment at 1050 °C for 1h was done to remove work-hardening effects after cold deformation. Also, for the investigation of microstructure and texture, optical and scanning electron microscopy was used, and also for studying macro-texture, X-ray diffraction method was used. Investigation of pole figures and orientation distribution function shows that grains have preferred orientation in the rolling direction after cold rolling deformation. In contrast, grains have random orientation in the homogenized and annealed specimens. Also, the copper component was dominated after cold rolling, while the cubic component was dominated in the homogenized specimen. Furthermore, copper component led to low ductility and improved the mechanical properties of alloy. Also, after annealing heat treatment, the copper component was removed, and the intensity of other components was decreased except the cubic component and formation of cubic component after annealing heat treatment in this alloy led to improving the ductility and decreasing mechanical properties.

metallurgy & metallurgical engineering