Microstructure, Texture and Magnetic Properties of Strip Casting Fe–6.2 Wt%si Steel Sheet

Hai-Tao Liu,Zhen-Yu Liu,Yi-Qing Qiu,Yu Sun,Guo-Dong Wang
DOI: https://doi.org/10.1016/j.jmatprotec.2012.04.015
IF: 6.3
2012-01-01
Journal of Materials Processing Technology
Abstract:An Fe–6.2 wt%Si strip with equiaxed grains and mild {0 0 1}〈0 v w〉 fiber texture was produced by twin-roll strip casting process. Then the as-cast strip was treated with or without the hot rolling prior to the warm rolling and annealing. When the hot rolling was not introduced, a fine and heterogeneous warm-rolled microstructure was produced and led to a fine recrystallization microstructure and very weak {0 0 1}〈0 v w〉 fiber texture in the annealed sheets. When the hot rolling was introduced, a coarse and homogeneous warm-rolled microstructure was produced and led to a very coarse recrystallization microstructure and much stronger {0 0 1}〈0 v w〉 fiber texture in the annealed sheets. The annealed sheets with hot rolling showed a higher magnetic induction and a higher core loss than those without hot rolling.
What problem does this paper attempt to address?