Abstract:In this paper, Fe-3%Si ultra-thin ribbons prepared by the planar flow casting (PFC) technique were subjected to temper rolling and annealing treatments. The microstructure and texture evolution during this process were examined through experimental measurements coupled with crystal plasticity finite element (CPFE) simulation to assess the feasibility of preparing ultra-thin non-oriented silicon steel using PFC ribbons. The results indicate that the PFC ribbons exhibit a significant columnar crystal structure, and {001}-oriented grains comprise over 30%. After being annealed, the grains with different orientations grew uniformly, the texture components were basically unchanged, and the {001} texture was well preserved. When annealing was carried out after temper rolling with a reduction rate of 7%, uneven grain growth was observed, and the growth tendency of the {001} grains, especially, surpassed that of the {111} grains, with an elevated temperature which peaked at 950 °C, where the proportion of {001} grains was maximal. When being annealed after temper rolling to 15%, grains of other orientations showed significant growth at each temperature, while the {001} grains did not show an obvious growth advantage. Utilizing the CPFE, the deformation-stored energy distribution of each characteristic-oriented grain was simulated, and it was shown that compared to the 15% rolling reduction rate, the deformation-stored energy accumulation of {001}-oriented grains after being rolled to 7% reduction was significantly lower than that of {111}-oriented grains. It suggests that the larger stored energy difference makes {001} grains show a stronger growth advantage based on the SIBM mechanism during annealing, after being rolled with a reduction rate of 7%. Overall, for the synergistic optimization of microstructure and texture, rolling with a 7% reduction rate followed by annealing at 950 °C in a hydrogen atmosphere is most advantageous.

Fabrication of high permeability non-oriented electrical steels by increasing 〈001〉 recrystallization texture using compacted strip casting processes

Microstructure and texture evolution of thin-gauge non-oriented silicon steel with high permeability produced by twin-roll strip casting

Development of Λ-Fiber Recrystallization Texture and Magnetic Property in Fe–6.5wt% Si Thin Sheet Produced by Strip Casting and Warm Rolling Method

Characterization of microstructure, texture and magnetic properties in twin-roll casting high silicon non-oriented electrical steel

Microstructure, texture and magnetic properties of strip-cast 1.3% Si non-oriented electrical steels

Microstructure and texture evolution of strip casting 3 wt% Si non-oriented silicon steel with columnar structure

Texture Evolution during Recrystallization and Grain Growth in Non-Oriented Electrical Steel Produced by Compact Strip Production Process

Effects of rolling temperature on microstructure, texture, formability and magnetic properties in strip casting Fe-6.5wt% Si non-oriented electrical steel

Fabrication of high-performance low silicon non-oriented electrical steels by a new method: Low-finishing-temperature hot rolling combined with batch annealing

Effect of Cold Rolling Process on Microstructure, Texture and Properties of Strip Cast Fe-2.6%Si Steel

A comprehensive study on texture evolution and recrystallization mechanism of Fe-4.5 wt% Si with strong {114}

Texture Development and Formability of Strip Cast 17% Cr Ferritic Stainless Steel

Dislocation Strengthening and Texture Evolution of Non-Oriented Fe-3.3 wt% Si Steel in Double Cold Rolling

Microstructure and Texture Evolution of Strip-Cast and Hot-Rolled Fe-3 %si Steel Sheet

Microstructure, texture and magnetic properties of the semi-processed strip-cast non-oriented electrical steel

Ultrastrong {100} texture in twin-roll strip cast non-oriented electrical steel through two-step annealing

Development of microstructure and texture in strip casting grain oriented silicon steel

Tracing the recrystallization of warm temper-rolled Fe–6.5 wt% Si non-oriented electrical steel using a quasi in situ EBSD technique

Study on Microstructure and Texture of Fe-3%Si Ultra-Thin Ribbons Prepared by Planar Flow Casting

Significant effect of as-cast microstructure on texture evolution and magnetic properties of strip cast non-oriented silicon steel

Evolution of microstructure, texture and inhibitor along the processing route for grain-oriented electrical steels using strip casting