Ultrathin-gauge high silicon non-oriented electrical steel with high permeability and low core loss fabricated by optimized two-stage cold rolling method
Zhi-hong Li,Song-kang Xie,Guo-dong Wang,Hai-tao Liu
DOI: https://doi.org/10.1016/j.matchar.2021.111593
IF: 4.537
2022-01-01
Materials Characterization
Abstract:In the present work, the evolution of microstructure and texture and the resultant magnetic properties with different rolling reductions and intermediate annealing temperatures during two-stage cold rolling process were systematically studied. The one-stage cold rolling was also employed for comparison. It was found that finally annealed sheet fabricated by one-stage rolling exhibited pronounced α*-fiber ({h,1,1} < 1/h,1,2>) and γ-fiber (〈111〉//ND) textures. By contrast, the two-stage rolling significantly weakened the unfavorable γ-fiber texture and enhanced the λ-fiber (〈100〉//ND), Goss ({110} 〈001〉) and near-Brass ({110} 〈112〉) textures in final sheets. Meanwhile, the introduction of intermediate annealing reduced the grain boundary density and deformation stored energy in secondly cold-rolled microstructure. The nucleation rate of recrystallization was hence decreased, thereby increasing the final grain size. Increasing intermediate annealing temperature in two-stage rolling process further optimized the recrystallization texture and increased the final grain size. It is noted that the γ-fiber texture in final sheets was gradually decreased with the decrease of second rolling reduction, while the λ-fiber texture and grain size were both increased firstly and then decreased. Eventually, an optimized combination of magnetic properties (B50 = 1.709 T, P15/50 = 1.828 W/kg, P10/400 = 11.92 W/kg) was obtained via a higher intermediate annealing temperature (950 °C) and an appropriate second rolling reduction (75%). Furthermore, the deformation and recrystallization behaviors of specifically oriented grains (i.e., λ-, Goss and near-Brass grains) were discussed in detail.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing