Evolution of {0kl} 〈1 0 0〉 texture and microstructure in preparation of ultra-thin grain-oriented silicon steel

Li Meng,Ning Zhang,Bo Zhang,Cheng-xu He,Yu Han,Guang Ma,Xin Chen,Jia-xin Yang,Xiao-long Guo,Sheng Zhong

DOI: https://doi.org/10.1016/j.jmmm.2020.167590

IF: 3.097

2021-04-01

Journal of Magnetism and Magnetic Materials

Abstract:<p>In this paper, an ultra-thin grain-oriented silicon steel (UTGO steel) strip was prepared via rolling a commercial glassless grain-oriented silicon steel plate to 0.075mm and then annealing it at 850℃ for less than 30 min in a protective atmosphere. The resultant UTGO steel strip has magnetic induction B₈₀₀ higher than 1.80 T and iron loss P_1.5/400 lower than 12.0 W/kg. These superior magnetic properties are due to predominant {0kl}&lt;100&gt; texture and appropriate microstructure. The study shows that preferential {0kl}&lt;100&gt; nucleation occurs either inside shear bands or at in-grain deformation-induced boundaries. The nucleation behavior varies at different nucleation sites. Nuclei inside shear bands are denser and show preferential transitional orientation along {0kl}&lt;100&gt;, while new grains dispersed at in-grain split boundaries have shown orientations which are suggested to inherit corresponding initial grain orientation prior to rolling. Nucleation behavior is also highly dependent on the orientation of the roll-deformed matrix. Our study finds that shear banding nucleation of {0kl}&lt;100&gt; (including Goss and {021}&lt;100&gt;) is reduced when the orientation of the deformed matrix deviates from {111}&lt;112&gt;. With the extension of annealing time, the growth of {0kl}&lt;100&gt; nuclei in cluster is restricted because of orientation pinning effect, whereas the growth of grains with orientations other than {0kl}&lt;100&gt; is promoted. This phenomenon weakens the dominance of {0kl}&lt;100&gt; texture, causing deterioration in magnetic properties of the final silicon steel.</p>

materials science, multidisciplinary,physics, condensed matter