Abstract:High-strength prestressing cables exposed to high temperature result in the prestress loss, potentially leading to failure and even collapse of prestressing structures. This paper experimentally investigates thermal expansion of 1860 MPa steel wires and prestress loss of 1860 MPa twisted wire strands and parallel wire strands at elevated temperatures initially. Strands are localised heated in prestress loss tests. Different highest temperatures and initial prestress levels are considered. The test results show that EC2 underestimates the thermal strain of 1860 MPa steel wire at more than 450 °C. Prestress loss of the prestressing strand increases as the temperature increases. Cable types have little influence on the final prestress loss ratio. The strand with higher initial prestress level results in less final prestress loss ratio at less than 400 °C. A series fitting formulas of thermal strain, thermal expansion coefficient and final prestress loss ratio of prestressing strands are proposed. In addition, the finite element model of prestressing strand at elevated temperatures is established and validated. The numerical analysis shows that the temperature of the strand in non-heated region is significant, and the stress of the strand rises and then fall during heating stage, due to the balance between thermal expansion and degradation of mechanical properties. Finally, the analytical model of the prestress loss of the strands at elevated temperatures is proposed. The effect of thermal expansion, degradation of the mechanical properties and high-temperature creep of the strand in the heated region and non-heated region is considered respectively. Simplified method is obtained for more efficient computation. The analytical results have great agreement with the test results. The application of analytical method on practical engineering is discussed, and improved calculation equation is proposed for large span cables exposed to localised fire.

Mechanical properties and bonding strength of twisted wire strands at elevated temperatures

Effect of High Temperature Exposure and Strain Rate on Mechanical Properties of High-Strength Steel Rebars

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Al-clad Cu Bond Wires for Power Electronics Packaging: Microstructure Evolution, Mechanical Performance, and Molecular Dynamics Simulation of Diffusion Behaviors

Enhanced Tensile Properties And Fracture Reliability Of Cu-Based Amorphous Wires Via Pr-Doping

Elevated-temperature mechanical property and constitutive model of galvanized parallel wire strands

Prestress loss of twisted wire strands and parallel wire strands at elevated temperatures

Mechanical properties of butt weldments made with E5515-G electrodes at high temperature

High-temperature mechanical properties and failure modes of UHSS wire for cable-supported bridge

Mechanical Properties of Butt Weldments Made with Q345B Steel and E5015 Electrodes at Different Temperatures

Tensile strengths of super high-strength steel strand wire ropes and wire rope open swaged socket connections at fire and post fire

Effect of Welding Defects on Mechanical Properties of Welded Joints Subjected to Temperature

Relating Residual Stress and Microstructure to Mechanical and Giant Magneto-Impedance Properties in Cold-Drawn Co-based Amorphous Microwires

Microstructure evolution of high-strength and ultra-high-conductivity microfilament wire prepared by continuous deformation of single-crystal copper

Effect of Process Parameters on the Surface Quality, Microstructure and Properties of Pure Copper Wires Prepared by Warm Mold Continuous Casting

Quantitative Study on the Evolution of Microstructure, Strength, and Electrical Conductivity of the Annealed Oxygen‐Free Copper Wires

Fracture behavior of Grade 10.9 high-strength bolts and T-stub connections in fire

Post-fire mechanical properties of stainless steel cables

Effects of Heat Treatment Temperature on Microstructure and Properties of Wiredrawn Cu-12ag Filamentary Composite

Impact tension behavior of heavy-drawn nanocrystalline CoCrNi medium entropy alloy wire

Interfacial microstructure and thermal shock resistance of diffusion bonding ODS-W and molybdenum alloy by spark plasma sintering