Abstract:Hot isostatic pressing (HIP) is usually applied to reduce the defects including cracks and pores in the materials prepared by laser powder bed fusion (LPBF). In the present research, in order to improve the relative density and mechanical property, HIP was employed on the LPBF-processed Al-Cr-Fe-Ni-V high-entropy alloy (HEA) with microcracks and pores. The microstructure evolution and property improvement induced by HIP were investigated. In the LPBF-processed HEA, the microcracks were caused by residual stress and element segregation, and these microcracks as well as the pores reduced significantly after HIP treatments. Remarkably, HIP temperature has a more critical effect on the microcrack closure than the holding time, thus, microcracks and pores still existed after HIP-1 treatment (1273 K, 8 h), while HIP-2 treatment (1473 K, 4 h) could close the microcracks significantly. The crack closure was attributed to the interfacial diffusion of the alloying element under high temperature accompanied by high pressure, and the degree of element diffusion at both interfaces of the cracks determined the bonding strength after crack closure. Higher temperatures at high pressure induced more adequate element diffusion and higher bonding strength. The above high temperature and high pressure also induced the growth of the L1 2 phase and the precipitation of the B2 phase in HEA. Consequently, the tensile strength and elongation of the LPBF-processed HEA after HIP-2 treatment were simultaneously enhanced (80.7% and 222.5% higher than that of LPBF-processed HEA, respectively). This could be attributed to the combined effect of microcrack/pore closure and precipitation strengthening. The strengthening effect of the B2 phase and L1 2 phase accounted for 53% (dislocation by-pass mechanism) and 47% (dislocation shearing mechanism) of the total precipitation strengthening, respectively.

Micro-cracking, microstructure and mechanical properties of Hastelloy-X alloy printed by laser powder bed fusion: As-built, annealed and hot-isostatic pressed

Mechanical Properties and Fracture Behavior of Laser Powder-Bed-Fused GH3536 Superalloy

Microstructure and mechanical properties at room and elevated temperature of crack-free Hastelloy X fabricated by laser powder bed fusion

Hot-Cracking Mitigation and Microcrack Formation Mechanisms in Laser Powder Bed Fusion Processed Hastelloy X and Cantor High Entropy Alloys

Investigation of Microstructure and Failure Mechanisms at Room and Elevated Temperature of Hastelloy X Produced by Laser Powder-Bed Fusion

Dynamic strain aging and recrystallization mechanisms in laser powder bed melt printing of highly textured Hastelloy X

Microstructural Evolution of Post-Processed Hastelloy X Alloy Fabricated by Laser Powder Bed Fusion

The Microstructures and Mechanical Properties of a Welded Ni-Based Hastelloy X Superalloy

Oxidation behavior of Hastelloy X alloy fabricated by selective laser melting and subsequent hot isostatic pressing treatment

Tailoring the microstructure and mechanical properties for Hastelloy X alloy by laser powder bed fusion via scanning strategy

Simultaneously improved the strength and ductility of laser powder bed fused Al-Cr-Fe-Ni-V high-entropy alloy by hot isostatic pressing: Microcrack closure and precipitation strengthening

In-situ Study of Microstructure and Mechanical Properties of GH3536 Alloy Manufactured by Selective Laser Melting at 750 °C

Effect of temperature on the microstructure and tensile properties of micro-crack free hastelloy X produced by selective laser melting

Experimental Characterization and Strengthening Mechanism of Process-Structure-property of Selective Laser Melted 316 L

Microstructural Control Strategy Based on Optimizing Laser Powder Bed Fusion for Different Hastelloy X Powder Size

Recrystallization effect on surface passivation of Hastelloy X alloy fabricated by laser powder bed fusion

Pre-softening HIP Treatment Enabled Crack-Healing and Superior Mechanical Properties for René 142 Superalloy Fabricated Via Laser Powder Bed Fusion

High-temperature high cycle fatigue performance of laser powder bed fusion fabricated Hastelloy X: Study into the microstructure and oxidation effects

Synergic effects of scanning pattern and heat treatment on the microstructure-hot tensile behavior relationships of powder bed fusion-laser beam manufactured Hastelloy X

Microstructure and Mechanical Properties of Hastelloy-X Produced by Selective Laser Melting

High-Temperature Tensile Properties of Hastelloy X Produced by Laser Powder Bed Fusion with Different Heat Treatments