Oxidation behavior of Hastelloy X alloy fabricated by selective laser melting and subsequent hot isostatic pressing treatment

Hui Wang,Hong Wu,Yong Liu,Wenbin Qiu,Hao Deng,Lvjun Zhou,Longqing Chen
DOI: https://doi.org/10.1002/adem.202200369
IF: 3.6
2022-07-19
Advanced Engineering Materials
Abstract:Hastelloy X is a typical solid solution strengthening superalloy featured by good tolerance against oxidation and adequate mechanical and creep properties at 900°C. However, current works about Ni‐based superalloys mainly focus on the relationship between microstructure and mechanical performance at high temperature regions, leaving the failure mechanism under the circumstance of oxidation as an open issue. In this work, we investigated the effects of the microstructure on the high‐temperature oxidation behavior and mechanical properties of Hastelloy X alloys prepared by selective laser melting (SLM) technique and hot isostatic pressing (HIP), respectively. The experimental results showed the existence of a large number of micro‐cracks in the SLM samples during oxidation at 900°C, which could contribute to increased oxidation weight gain and ease of oxide layer exfoliation. With the assistance of HIP, thermal cracks were effectively eliminated by the combination of better elemental homogeneity. The further improvement of oxidation resistance was found to result from the densification of Cr2O3 particles and the hindrance of oxygen diffusion. From the perspective of the application, this work provides valuable support for the explanations of the oxidation resistance and fracture mechanism of Hastelloy X superalloys in high‐temperature service environments. This article is protected by copyright. All rights reserved.
materials science, multidisciplinary
What problem does this paper attempt to address?