Mechanical properties and precipitation behavior of the heat-treated wire + arc additively manufactured 2219 aluminum alloy

Yinghui Zhou,Xin Lin,Nan Kang,Weidong Huang,Zhennan Wang

DOI: https://doi.org/10.1016/j.matchar.2020.110735

IF: 4.537

2021-01-01

Materials Characterization

Abstract:<p>The dense 2219 Al alloy was successfully fabricated by the Wire + Arc additive manufacturing (WAAM) technology. It was subsequently processed through solution and aging (T6) heat treatment to improve its performance. There were some θ' phase precipitated because of the thermal cycling during the WAAM forming process. Then, the supersaturation of copper in the α-Al matrix was reduced. The influence of solution temperature on the precipitation behavior of the θ″ phase and the microstructure evolution were investigated in detail. The experimental and calculative results demonstrate that the precipitation strengthening of the θ″ phase improves with the increasing solution temperature, and the strengthening contribution of θ″ phase is 202.1 MPa, 165.2 MPa, and 150.3 MPa corresponding to the solution temperature at 540 °C, 530 °C, and 520 °C, respectively. The average ultimate tensile strength, yield strength, elongation, and micro-hardness of the WAAM processed samples were obtained after T6 treatment with 540 °C, 45 min/Water quenching +180 °C, 6 h/Water quenching, which is 397 ± 4 MPa, 303 ± 5 MPa, 5.3 ± 1%, and 139 ± 6 HV respectively. Compared to the casting + T6 treated 2219 Al alloy, the samples in this research present a similar tensile strength and slightly lower ductility.</p>

materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing

What problem does this paper attempt to address?

### Problems Addressed by the Paper

This paper aims to explore the mechanical properties and precipitation behavior of 2219 aluminum alloy prepared by Wire + Arc Additive Manufacturing (WAAM) technology during the heat treatment process. Specifically, the paper focuses on the following aspects:

1. **Improvement of Mechanical Properties**: Investigate the improvement of mechanical properties of 2219 aluminum alloy prepared by WAAM through solution treatment and aging treatment, particularly tensile strength, yield strength, elongation, and microhardness.

2. **Impact on Precipitation Behavior**: Analyze the impact of different solution temperatures on the precipitation behavior of the θ″ phase and the evolution of the microstructure. The θ″ phase is the main strengthening phase of 2219 aluminum alloy, and its size, volume fraction, and distribution significantly affect the alloy's mechanical properties.

3. **Optimization of Heat Treatment Parameters**: Determine the most suitable solution temperature through experiments and theoretical calculations to maximize the precipitation strengthening effect of the θ″ phase, thereby improving the overall performance of the alloy.

### Main Findings

- **Effect of Solution Temperature**: As the solution temperature increases from 520°C to 540°C, the supersaturation of copper in the α-Al matrix increases, leading to more θ″ phase precipitation and significantly enhanced strengthening effect. 540°C is an appropriate solution temperature.
- **Improvement of Mechanical Properties**: After solution treatment at 540°C and aging treatment at 180°C, the tensile strength of the samples reached 397±4 MPa, the yield strength reached 303±5 MPa, the elongation reached 5.3±1%, and the microhardness reached 139±6 HV.
- **Comparison with Cast Alloy**: Compared with the traditional cast + T6 treated 2219 aluminum alloy, the samples prepared by WAAM have similar tensile strength but slightly lower plasticity.

### Conclusion

- **Precipitation Strengthening Effect**: The precipitation strengthening effect of the θ″ phase increases with the rise in solution temperature. When the solution temperature is 540°C, the samples can obtain a large number of nano-sized and uniformly distributed θ″ phases, which is the most suitable solution temperature.
- **Effect of Copper Content**: When the copper content dissolved in the matrix is 6.95%, 7.07%, and 7.64%, respectively, after aging treatment at 180°C, the yield strength increments of the θ″ phase are 150.3 MPa, 165.2 MPa, and 202.1 MPa, respectively.

This study provides important references for optimizing the heat treatment process of 2219 aluminum alloy prepared by WAAM, which helps to further enhance its mechanical properties.