Abstract:To ensure the high-temperature stability of a bondline under next-generation power devices such as SiC semiconductors, a die bonding test was performed by transient liquid-phase (TLP) sinter-bonding using a Sn-coated Cu (Cu@Sn) particle-based preform. Compared to the existing 20 min-bonding result using a 30 μm Cu@Sn particle-based preform, a 5 μm Cu@Sn particle-based preform was used to significantly reduce the bonding time to 5 min, and the optimal levels of the amount of Sn in the Cu@Sn particles, the thicknesses of Sn surface finish layers on the chip and substrate, and compression pressure during the bonding were investigated. The Sn content in the Cu@Sn particles significantly changed the microstructure, including the porosity of the prepared preform. The preform porosity of 0.01% was confirmed after the formation of sufficient Sn shells with an average thickness of about 602 nm at Sn 30 wt%. In addition, in the preform with Sn 30 wt% content, the Sn phase was almost depleted after 3 min after annealing at 250 °C. The Sn finish layer was evaluated in the thickness range of 0.63−4.12 μm, and it was observed that the shear strength of the formed bondline tended to increase with increasing pressure for all Sn layer thicknesses. In particular, when the bonding was carried out at a pressure of 2 MPa using a dummy Cu chip and substrate coated with a 1.53 μm thick Sn layer, the best shear strength value of 36.89 MPa was achieved. In this case, all the Sn phases transformed into intermetallic compound phases of Cu 6 Sn 5 and Cu 3 Sn, and all the phases formed within the bondline, including Cu, exhibited high melting-point characteristics. Therefore, it was determined that there would be no remelting of the bondline or a drastic decrease in mechanical properties in a high-temperature environment below 300 o C, as initially intended. By increasing the content of the Sn shell up to 30 wt%, it was possible to achieve a nearly full density (porosity: 0.3%) bondline structure, due to the rearrangement behavior of particles, by maintaining liquid Sn for a long time during the bonding process. In conclusion, the optimal Sn finish thickness was determined to be at the level of 1.5 μm, and the optimal pressure was at the level of 2 MPa. The short bonding time of 5 min represents a significant advance in TLP bonding processes, and it is expected to contribute to a substantial improvement in the die bonding of future SiC power devices.

Fabrication of Sn-plated Cu foam for high-efficiency transient-liquid-phase bonding

Facile preparation of Cu foam/Sn composite preforms for low-temperature interconnection of high-power devices

Novel and fast transient liquid phase bonding using etched Cu foam/Sn–3.0Ag–0.5Cu composite solder preform

Novel transient liquid phase bonding through capillary action for high-temperature power devices packaging

Fabrication of cu@sn core-shell structure preform and application in high temperature bonding

Low-Temperature Transient Liquid Phase Bonding Technology via Cu Porous-Sn58Bi Solid–Liquid System under Formic Acid Atmosphere

Transient Liquid-Phase Sinter-Bonding Characteristics of a 5 um Cu@Sn Particle-Based Preform for High-Speed Die Bonding of Power Devices

Cu@Sn Core–Shell Structure Powder Preform for High-Temperature Applications Based on Transient Liquid Phase Bonding

Interconnection method based on Cu-foam/Sn composite preform for high-temperature applications

Fabrication of Cu@Sn Core-Shell Structured Particles and the Application in High Remelting Temperature Bonding

Low Temperature Cu-Cu Bonding Using an Intermediate Sacrificial Sn Layer

Microstructure Characterization and Mechanical Behavior for Ag3sn Joint Produced by Foil-Based Tlp Bonding in Air Atmosphere

Sn-enhanced high-temperature reliability of Cu/Nano-Ag/Cu joint via transient-liquid-phase bonding

Low-Temperature Cu-Cu Bonding Process Based on the Sn-Cu Multilayer and Self-Propagating Reaction Joining

Fine-Pitch Cu-Sn Transient-Liquid-Phase Bonding Based on Reflow and Pre-Bonding

Interfacial Reaction and Mechanical Properties for Cu/Sn/Ag System Low Temperature Transient Liquid Phase Bonding

Wafer-Level Hermetic Package by Low-Temperature Cu/Sn TLP Bonding with Optimized Sn Thickness

Effect of Powders on Microstructures and Mechanical Properties for Sn–Ag Transient Liquid Phase Bonding in Air

Novel Sn-Cu Based Composite Solder Preforms Capable of Low Temperature Reflow for Die Attachment of High Temperature Power Electronics and the Transient Liquid Phase Bonding Process

Fabrication of High-Temperature-resistant Bondline Based on Multilayer Core–shell Hybrid Microspheres for Power Devices

Low Temperature Cu-Sn Bonding By Isothermal Solidification Technology