Abstract:In this work, an alkali melting‐pickling assisted solid phase synthesis method of S‐1 zeolite molecular sieve with excellent adsorption properties for CO2 was successfully developed by using solid waste fly ash. SiO2 with a purity of up to 97.84% was successfully extracted by using alkaline fusion activation, high temperature calcination and pickling. The CO2 adsorption capacity of the prepared SiO2 was 0.51 mmol/g at 298 K and 1 bar. Silicalite‐1 molecular sieve was prepared by solid phase synthesis method using SiO2 extracted from fly ash as silicon source. The results showed that the prepared Silicalite‐1 had good morphology and relatively high crystallinity. The specific surface area is 623.30 m2/g, and the total pore volume is 0.31 cm3/g. In addition, the adsorption capacity of CO2 was 2.05 mmol/g at 298 K and 1 bar. Compared with the prepared SiO2, the adsorption capacity of CO2 by Silicalite‐1 molecular sieve increased by four times. Moreover, under the test condition of 298 K, it has a high selectivity coefficient for CO2/N2 mixed gas, and after 10 times of adsorption‐desorption cycle tests, the adsorption capacity of Silicalite‐1 molecular sieve for CO2 does not change significantly, and its adsorption rate can still be as high as 89.31%. The results indicate that Silicalite‐1 molecular sieve prepared by solid phase synthesis method has good adsorption selectivity and adsorption–desorption cycle regeneration stability, and can be used in the field of CO2 adsorption, separation and purification. © 2024 Society of Chemical Industry and John Wiley & Sons, Ltd.

Synthesis and CO 2 adsorption performance of high Si/Al ratio DDR zeolites prepared from silica fume

An Oriented, Siliceous Deca-Dodecasil 3r (ddr) Zeolite Film for Effective Carbon Capture: Insight into Its Hydrophobic Effect

Efficient Synthesis of All-silica DDR Zeolite

Growth Study of Hierarchical Pore SSZ-13 Molecular Sieves with Improved CO2 Adsorption Performance

DDR-type Zeolite Membrane Synthesis, Modification and Gas Permeation Studies

Hierarchical Porous Nanosilica Derived from Coal Gasification Fly Ash with Excellent CO2 Adsorption Performance

Enhanced CO2 Adsorption Performance on Hierarchical Porous ZSM-5 Zeolite

Synthesis of zeolite molecular sieve 13X from coal-fired slag for efficient room temperature CO2 adsorption

Fast synthesis of thin all-silica DDR zeolite membranes with inorganic base as mineralizing agent for CO2-CH4 separation

Controllable Preparation of Cubic Zeolite A and Application of Langmuir Model in Carbon Dioxide Adsorption

Regulating the Si/Al ratio of GIS zeolite with bulky primary particles for selective CO 2 capture from hydrocarbons

Preparation of ZSM-5 molecular sieve by diatomaceous earth in-situ crystallization

Study on the Synthesis of High-Purity γ-Phase Mesoporous Alumina with Excellent CO2 Adsorption Performance via a Simple Method Using Industrial Aluminum Oxide as Raw Material

Synthesis of ordered mesoporous silica from biomass ash and its application in CO2 adsorption

Organic template-free synthesis of K-SAPO-34 zeolite for efficient CO 2 separation

Solid‐phase synthesis of silicalite‐1 molecular sieve based on fly ash and its CO2 adsorption performance

Synthesis of mesoporous sodalite from coal-fired slag for CO2 capture

Effect of Different Silicon Sources on CO2 Adsorption of Li4SiO4 at High Temperature

Rational Synthesis of Chabazite (CHA) Zeolites with Controlled Si/Al Ratio and Their CO2 /CH4 /N2 Adsorptive Separation Performances

Synthesis of Cu-SSZ-13 from Zeolite Analcime Derived from Solid Waste and Natural Minerals for Selective Catalytic Reduction of NO

Enhancement of Carbon Dioxide Adsorption Over Alkali-cations Borosilicate ZSM-5 Zeolite