Energy storage performance of flexible NKBT/NKBT-ST multilayer film capacitor by interface engineering
Jin Qian,Yajie Han,Changhong Yang,Panpan Lv,Xiaofang Zhang,Chao Feng,Xiujuan Lin,Shifeng Huang,Xin Cheng,Zhenxiang Cheng
DOI: https://doi.org/10.1016/j.nanoen.2020.104862
IF: 17.6
2020-08-01
Nano Energy
Abstract:<p>Dielectric film capacitors with high energy density (<em>W</em><sub>rec</sub>) and high efficiency (<em>η</em>) as well as good flexibility are highly desired in electrical power systems, which will be beneficial to the minimization and integration of next generation advanced flexible electronic devices. Here, lead free (Na<sub>0.8</sub>K<sub>0.2</sub>)<sub>0.5</sub>Bi<sub>0.5</sub>TiO<sub>3</sub>/0.6(Na<sub>0.8</sub>K<sub>0.2</sub>)<sub>0.5</sub>Bi<sub>0.5</sub>TiO<sub>3</sub>-0.4SrTiO<sub>3</sub> (NKBT/NKBT-ST)<sub>N</sub> multilayer films with different stacking periodic numbers (N = 2,3,6,8) were constructed on mica substrate by combining the ferroelectric NKBT with large polarization and relaxor ferroelectric NKBT-ST with high breakdown strength (<em>E</em><sub>b</sub>). Under a fixed film thickness, the <em>W</em><sub>rec</sub> and <em>η</em> can be optimized by interface engineering. A giant <em>W</em><sub>rec</sub> of ∼73.7 J cm<sup>−3</sup> and high <em>η</em> of ∼68.1% are simultaneously obtained in the NKBT/NKBT-ST multilayer film with N = 6. The energy storage behavior can be quite stable and reliable in a wide temperature (−50 °C–200 °C) and frequency (500 Hz-20 kHz) ranges and even after 10<sup>8</sup> cycles. Meanwhile, with the assistance of mica substrate, the designed film capacitor exhibits excellent bending endurance, i.e., the <em>W</em><sub>rec</sub> and <em>η</em> can maintain well even under a small bending radius of <em>r</em> = 2 mm or after 10<sup>4</sup> bending cycles at <em>r</em> = 4 mm. All these characteristics make this flexible multilayer film capacitor potential for future applications.</p>
materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology