Abstract:A series of mesoporous nanocrystalline Ce-Zr solid solutions with different Ce/Zr ratios were successfully synthesized by the evaporation-induced self-assembly strategy, and were employed as catalytic supports of CuO-based catalysts for CO oxidation. These supports and catalysts were systematically characterized by X-ray powder diffraction (XRD), N-2 physisorption, transmission electron microscopy (TEM), energy-dispersed spectroscopy (EDS) mapping, X-ray photoelectron spectroscopy (XPS), H-2 temperature programmed reduction (H2-TPR), CO2 temperature programmed desorption (CO2-TPD), etc. The catalytic performances toward CO oxidation had been carefully evaluated over these CuO-based catalysts. The effects of various influencing factors, such as the Ce/Zr ratio, mesostructure, redox properties of the support, CuO loading amount and calcination temperature, on the low-temperature catalytic activity had been carefully investigated. The results showed that the catalyst supported on the support with a Ce/Zr ratio of 80/20 exhibited the highest catalytic activity. It was also found that the Ce-Zr solid solution mesoporous catalysts exhibited much higher catalytic activity than the counterparts without evident mesostructure, demonstrating the advantages of the mesoporous catalysts by providing more accessible catalytically active sites. Besides, the mesoporous Ce-Zr solid solution-supported catalysts with excellent redox properties displayed much better catalytic performances than the commercial gamma-Al2O3-supported catalyst. The kinetic study also indicated that the apparent activation energy of the CO oxidation process was greatly affected by the Ce/Zr ratio, mesostructure, and redox properties of the support. Overall, the present CuO-based catalysts with mesoporous nanocrystalline Ce-Zr solid solutions as supports were considered as a series of promising catalysts for CO oxidation.

Copper-ceria solid solution with improved catalytic activity for hydrogenation of CO2 to CH3OH

Boosting the Catalytic Performance of CuO x in CO 2 Hydrogenation by Incorporating CeO 2 Promoters

An investigation of Zr/Ce ratio influencing the catalytic performance of CuO/Ce1-Zr O2 catalyst for CO2 hydrogenation to CH3OH

Copper-doped ZnO-ZrO2 solid solution catalysts for promoting methanol synthesis from CO2 hydrogenation

CO2 Hydrogenation to Methanol over Bimetallic Pd-Cu Catalysts Supported on TiO2-CeO2 and TiO2-ZrO2

In Situ Characterization of Cu/CeO2 Nanocatalysts for CO2 Hydrogenation: Morphological Effects of Nanostructured Ceria on the Catalytic Activity

Stabilizing Cu2+ Ions by Solid Solutions to Promote CO2 Electroreduction to Methane

Facilely fabricating mesoporous nanocrystalline Ce–Zr solid solution supported CuO-based catalysts with advanced low-temperature activity toward CO oxidation

Effect of Ce Modification on the Performance of CuLDH Catalyst for CO2 Hydrogenation to Methanol

Engineering Cu plus /CeZrOx interfaces to promote CO2 hydrogenation to methanol

Insight into the Synergism Between Copper Species and Surface Defects Influenced by Copper Content over Copper/Ceria Catalysts for the Hydrogenation of Carbonate

Effect of the nature of copper species on methanol synthesis from CO2 hydrogenation reaction over CuO/Ce0.4Zr0.6O2 catalyst

Copper–Cerium–Tin Oxide Catalysts for Preferential Oxidation of CO in Hydrogen: Effects of Synthesis Method and Copper Content

A dual-site Cu-ZnO/Cu@Si catalyst boosts CO2 hydrogenation to CH3OH

Hydrogenation of Co2 to Methanol over Cucetiox Catalysts

Preparation and properties of cerium modified Cu based catalysts for methanol synthesis

CO2 hydrogenation to CH4 over hydrothermal prepared ceria-nickel catalysts: Performance and mechanism study

A Ce-CuZn catalyst with abundant Cu/Zn-OV-Ce active sites for CO2 hydrogenation to methanol

CO2 hydrogenation to methanol promoted by Cu and metastable tetragonal Ce Zr O interface

Ceria engineering in nickel catalysts to improve CH 4 selectivity and yield for CO methanation

PdCu supported on dendritic mesoporous CexZr1-xO2 as superior catalysts to boost CO2 hydrogenation to methanol