Abstract:A series of mesoporous nanocrystalline Ce-Zr solid solutions with different Ce/Zr ratios were successfully synthesized by the evaporation-induced self-assembly strategy, and were employed as catalytic supports of CuO-based catalysts for CO oxidation. These supports and catalysts were systematically characterized by X-ray powder diffraction (XRD), N-2 physisorption, transmission electron microscopy (TEM), energy-dispersed spectroscopy (EDS) mapping, X-ray photoelectron spectroscopy (XPS), H-2 temperature programmed reduction (H2-TPR), CO2 temperature programmed desorption (CO2-TPD), etc. The catalytic performances toward CO oxidation had been carefully evaluated over these CuO-based catalysts. The effects of various influencing factors, such as the Ce/Zr ratio, mesostructure, redox properties of the support, CuO loading amount and calcination temperature, on the low-temperature catalytic activity had been carefully investigated. The results showed that the catalyst supported on the support with a Ce/Zr ratio of 80/20 exhibited the highest catalytic activity. It was also found that the Ce-Zr solid solution mesoporous catalysts exhibited much higher catalytic activity than the counterparts without evident mesostructure, demonstrating the advantages of the mesoporous catalysts by providing more accessible catalytically active sites. Besides, the mesoporous Ce-Zr solid solution-supported catalysts with excellent redox properties displayed much better catalytic performances than the commercial gamma-Al2O3-supported catalyst. The kinetic study also indicated that the apparent activation energy of the CO oxidation process was greatly affected by the Ce/Zr ratio, mesostructure, and redox properties of the support. Overall, the present CuO-based catalysts with mesoporous nanocrystalline Ce-Zr solid solutions as supports were considered as a series of promising catalysts for CO oxidation.

Preparation and properties of cerium modified Cu based catalysts for methanol synthesis

Effect of Ce Modification on the Performance of CuLDH Catalyst for CO2 Hydrogenation to Methanol

Methanol Synthesis from CO2 Hydrogenation over CuZnCeTi Mixed Oxide Catalysts

A Ce-CuZn catalyst with abundant Cu/Zn-OV-Ce active sites for CO2 hydrogenation to methanol

[Ce3+-OV-Ce4+] Located Surface-Distributed Sheet Cu-Zn-Ce Catalysts for Methanol Production by CO2 Hydrogenation

Engineering Cu plus /CeZrOx interfaces to promote CO2 hydrogenation to methanol

Synergistic Effect of Catalytic Action of Copper and Cerium in the Oxidation of CO on Modified Zeolites Cu/Ce/ZSM-5

Effect of the Zn/Ce ratio in Cu/ZnO–CeO 2 catalysts on CO 2 hydrogenation for methanol synthesis

Highly efficient CO2 hydrogenation to methanol over Cu–Ce1-xZrxO2 catalysts prepared by an eco-friendly and facile solid-phase grinding method

Facilely fabricating mesoporous nanocrystalline Ce–Zr solid solution supported CuO-based catalysts with advanced low-temperature activity toward CO oxidation

Methanol Synthesis Using Copper Catalysts Supported on CeO2−Al2O3 Mixed Oxide

Comparative Study on the Effect of Cerina and Alumina on the Catalytic Activity of CuO-ZnO Based Catalyst in CO2 Hydrogenation to Methanol

Promoting effect of an aluminum emulsion on catalytic performance of Cu-based catalysts for methanol synthesis from syngas

Mesoporous Ce-Zr Solid Solutions Supported Ni-based Catalysts for Low-Temperature CO2 Methanation by Tuning the Reaction Intermediates

Preparing methods of CuO/ZnO/Al2O3 catalysts for the synthesis of methanol

Ceria engineering in nickel catalysts to improve CH 4 selectivity and yield for CO methanation

Cu/ZnO/CeO2 Supported on MOF-5 as a Novel Catalyst for the CO2 Hydrogenation to Methanol: A Mechanistic Study on the Effect of CeO2 and MOF-5 on Active Sites

Synthesis of Cu-Ce0.8Zr0.2O2 catalyst by ball milling for CO2 reforming of ethanol

CO2 hydrogenation to methanol promoted by Cu and metastable tetragonal Ce Zr O interface

Hydrogenation of Co2 to Methanol over Cucetiox Catalysts

A High Activity Cu/ZnO/Al2O3 Catalyst for Methanol Synthesis: Preparation and Catalytic Properties