Very high cycle fatigue behaviors of GH4169 superalloy at room and high temperatures

Zhen Zhang,Zhenjie Teng,Jingyu Wang,Zhiyong Huang,Sebastian Münstermann

DOI: https://doi.org/10.1111/ffe.13700

2022-04-09

Abstract:Fatigue & Fracture of Engineering Materials & Structures, EarlyView.

materials science, multidisciplinary,engineering, mechanical

What problem does this paper attempt to address?

Effect of Initial Overload on the Low Cycle Fatigue Life of Gh4169 Alloy at Different Temperatures

Menglong Fan,Mingmin Qu,Chuanyong Chen,Haijun Xuan,Hailong Qin,Songyi Shi,Zhongnan Bi,Weirong Hong

DOI: https://doi.org/10.1016/j.ijfatigue.2024.108424

IF: 5.489

2024-01-01

International Journal of Fatigue

Abstract:In this paper, the effect of initial overload on the low cycle fatigue life of GH4169 alloy at different temperatures was studied. The plate specimen with a central hole was designed to perform low cycle fatigue tests at 20 degrees C, 500 degrees C and 650 degrees C with variable initial overloads. Results showed that the subsequent crack propagation rate depended on both overload ratio and following test temperature, and excessive overload treatment would also damage the surface or internal grains of the specimens through fracture characteristics under SEM. A finite element model was adopted to analyze the residual stress and stress-strain field at the edge of the central hole. Then, the stress and strain data were input to three strain-based model to predict the fatigue life of GH4169 alloy considering residual and mean stresses. Based on the combination of the experimental results and model prediction, the suggestion to improve the fatigue life of GH4169 alloy by initial overload can be put forward as following: a single initial overload makes the maximum local stress reach 90 %-93.5 % of the true ultimate stress of the material, so as to maximize its fatigue life.
Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Duyi Ye,Dehai Ping,Zhenlin Wang,Haohao Xu,Xiaoyu Mei,Changwei Xu,Xiaolin Chen

DOI: https://doi.org/10.1016/j.msea.2004.01.045

2004-01-01

Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.
Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Duyi Ye

DOI: https://doi.org/10.1016/j.ijfatigue.2005.01.014

IF: 5.489

2005-01-01

International Journal of Fatigue

Abstract:A series of experiments, including constant amplitude low-cycle fatigue tests, uniaxial tension failure tests, TEM observations and SEM examinations, were carried out to investigate the effect of cyclic straining at a temperature of 538°C on the static mechanical properties, the deformation microstructures and the fracture behavior of nickel-base superalloy GH4145/SQ. The change characteristics of the various basic static mechanical property parameters, such as the yield strength (σ0.2), the ultimate strength (σb), the modulus of elasticity (E), the reduction of area (φf), the elongation (δ) and the strain-hardening exponent (n), during elevated-temperature low-cycle fatigue of the alloy were obtained experimentally and their micromechanisms were further discussed through analyzing both deformation microstructures and fracture features of the cyclically deformed specimens. A composite static mechanical property parameter called static toughness (Ut) was proposed to characterize comprehensively the variation of the various basic static mechanical property parameters (σ0.2, σb, φf and n), and an approximate formulation describing the exhaustion of the static toughness during high-temperature fatigue failure process was constructed. A quantitative correlation between the exhaustion of the static toughness and the dissipation of the cyclic plastic strain energy during the course of high-temperature fatigue failure of the current alloy was developed in theory and further verified in experiment.
High-temperature Oxidation Behavior of AlCoCrCuFeNi High-Entropy Alloy by Selective Laser Melting

Ni Haohan,Zeng Qi,Zhang Kai,Tian Yanzhong,Wang Jiangwei

2023-01-01

Rare Metal Materials and Engineering

Abstract:Laser powder-bed fusion (L-PBF) technology possesses unique advantages in building complex-shape alloys. The microstructure and high temperature low-cycle fatigue behavior of L-PBFed GH3536 superalloy at 855 degrees C were investigated, and the influence of heat treatment on microstructure and fatigue performance was revealed. By combining different fatigue life prediction models, the fatigue damage behavior of L-PBFed GH3536 superalloy at various strain amplitudes was discussed. These results are important for high temperature low-cycle fatigue life prediction and application of additive manufactured metal part.
High-Temperature Low-Cycle Fatigue Properties of GH4169 Ni-based Superalloy

Liang-liang YAO,Xian-cheng ZHANG,Feng LIU,Shan-tung TU,Cong MA

DOI: https://doi.org/10.11973/jxgccl201604007

2016-01-01

Abstract:The total strain controlled high-temperature low-cycle fatigue experiments were conducted on the domestic GH4169 Ni-based superalloy.The fatigue properties of the alloy were studied and the fracture morphology was analyzed.The results show that the tested alloy had a superior low-cycle fatigue performance at elevated temperature,which was similar to that of imported Inconel 718 Ni-based alloy,but lower than the fatigue life of the Inconel 718 alloy at a relatively low total strain range.The cyclic stress softening behavior of the alloy was presented at different total strain ranges.The fatigue fractures of the alloy specimens showed a character of multi-crack sources and the crack source amounts decreased with the decrease of the total strain range and the prolonging of the fatigue life.The fatigue cracks all initiated at the specimen surface,and when propagated in an intergranular mode to a certain radial depth,showed a transgranular propagation characteristic.
Crack initiation mechanisms and life prediction of GH4169 superalloy in the high cycle and very high cycle fatigue regime

Zhi Qin,Bin Li,Chen Chen,Tianyue Chen,Rui Chen,Han Zhang,Hongqian Xue,Changfeng Yao,Liang Tan

DOI: https://doi.org/10.1016/j.jmrt.2023.07.196

IF: 6.267

2023-07-01

Journal of Materials Research and Technology

Abstract:In this study, the high cycle and very high cycle fatigue behavior of the GH4169 superalloy was investigated. The results of the fatigue tests demonstrated that failures in the high cycle fatigue regime were initiated from the material surface, whereas failures in the very high cycle fatigue regime had two competing modes of crack initiation: surface and internal. The fatigue fracture analysis revealed a quasi-cleavage fracture mode with facets for internal crack initiation. Additionally, the electron backscatter diffraction (EBSD) results indicated that the dislocations located at the internal twin boundaries of the material were preferentially activated under fatigue cyclic loading, resulting in significant strain localization at the twin boundaries. The {111} <110> slip systems with high Schmid factors had a higher probability of activation. The stress intensity factor (SIF) estimated based on rough area (RA) and facet sizes correspond to the fatigue long crack and short crack growth thresholds of the material, respectively. Finally, a modified FIP fatigue life prediction model was proposed based on the microstructure of crystallographic facets, and the results from experiment and the model prediction were found to be in good agreement.

materials science, multidisciplinary,metallurgy & metallurgical engineering
Interior long‐life‐fatigue cracking behavior and life prediction of a selective laser melted GH4169 superalloy at different temperatures and stress ratios

Rui Sun,Wei Li,Yucheng Zhang,Ping Wang,Tianyi Hu,Muhammad Imran Lashari,Tatsuo Sakai,Wen Zhang

DOI: https://doi.org/10.1111/ffe.13691

2022-03-23

Abstract:Fatigue & Fracture of Engineering Materials & Structures, EarlyView.

materials science, multidisciplinary,engineering, mechanical
High Temperature Low Cycle Fatigue Behavior of GH4742 Alloy

He-yong Qin,Gang Chen,Qiang Zhu,Chuan-jie Wang,Peng Zhang

DOI: https://doi.org/10.1016/s1006-706x(15)30039-x

2015-01-01

Abstract:High temperature low cycle fatigue tests on GH4742 supcralloy were studied under the total strain-controlled conditions at 650 °C. Combined with fatigue test data, fatigue properties of the alloy were analyzed. Fracture morphology and dislocation structure were observed by scanning electron microscopy and transmission electron microscopy. The results showed that fatigue life and fatigue resistance of GH4742 alloy decreased significantly with increasing total strain amplitude. The cyclic hardening, cyclic softening and cyclic stability phenomena of the alloy occurred during the low cycle fatigue process. The increasing total strain amplitude is conducive to the formation of γ′ phase. Fatigue crack propagation is controlled jointly by ductile and brittle fracture. Inhomogeneous deformation and deformation restricted in slip bands are the main reasons for the reduction of fatigue life of GH4742 alloy.
Microstructures' Effects on High Temperature Fatigue Failure Behavior of Typical Superalloys

L. N. Zhang,P. Wang,J. X. Dong,M. C. Zhang

DOI: https://doi.org/10.1016/j.msea.2013.08.065

IF: 6.044

2013-01-01

Materials Science and Engineering A

Abstract:This work examines the influence of microstructures on the fatigue failure behavior of the typical superalloys, GH864 and FGH96. A series of heat treatments were carried out to vary the grain size, the precipitation of carbide, and the γ′ phase. The fatigue failure behavior at 650°C is demonstrated by crack growth tests, both allowing a 90s dwell time and omitting any dwell time. Results from the as-received materials reveal four periods in the whole failure process: incubation, initiation, propagation, and instant fracture. The resistance of each period can be evaluated according to its proportion of the whole fatigue failure process. The alloy GH864, for example, shows an intersection of crack initiation and propagation when the solution temperature is around 1046°C or the carbide continuous coefficient (fc) is close to 0.56. An optimum point should exist where the strengthening effects of grain size and carbide precipitation achieve perfect matching for a normal alloy. The smaller sizes of secondary γ′ (γII′) and tertiary γ′ (γIII′) phases do present better crack growth resistance in their fatigue tests conducted without dwell time. The superior crack growth resistance of butterfly-shaped γII′, as compared to octagonally shaped γII′, indicates the influence of morphology on crack growth behavior. Moreover, the comprehensive parameter σs/(1−ψ) offers a helpful evaluation tool for determining crack growth resistance; its application is confirmed by experiments. All of these results produce not only a method for evaluating the life of engineering metals, but also provide a standard for designing highly damage-tolerant superalloys.
Combined high and low cycle fatigue analysis of FGH96 alloy under high temperature conditions

L. Liu,H.S. Gao,J.D. Wang,C.J. Zhang,Z.X. Wen,Z.F. Yue

DOI: https://doi.org/10.1016/j.mtcomm.2024.108053

IF: 3.8

2024-01-15

Materials Today Communications

Abstract:The FGH96 alloy as a common material for preparing turbine discs, can withstand high- and low-cycle combined loading during service, which significantly affects its fatigue performance. In this work, the combined high and low cycle fatigue (CCF) behavior of the FGH96 alloy was explored at various low cycle stress amplitudes (600, 630, 650, 680, and 700 MPa) using a self-improved experimental platform at a high temperature of 650 °C. The results indicate that increasing the amplitude of the low-cycle stress decreases the service endurance of the FGH96 alloy at CCF condition. Under the same low cycle stress amplitude, its CCF life of alloy is lower than the pure low cycle fatigue life. A fatigue service life prediction model, grounded in the theory of crystal plasticity, has been developed to assess the combined fatigue service life across different low-cycle stress amplitudes. A comparison between the predicted and actual lifespan showed that the predicted lifetime fell within a range three times the scattering band.

materials science, multidisciplinary
Competitive Fracture Mechanism and Microstructure‐Related Life Assessment of GH4169 Superalloy in High and Very High Cycle Fatigue Regimes

Muhammad Imran Lashari,Cheng Li,Asif Mahmood,Wei Li

DOI: https://doi.org/10.1111/ffe.14451

IF: 3.373

2024-10-10

Fatigue & Fracture of Engineering Materials & Structures

Abstract:High and very high cycle fatigue tests were performed to examine the microstructure and fracture mechanism of GH4169 superalloy in combination with techniques including electron‐backscatter diffraction (EBSD). Fractographic analysis revealed that surface failures are induced by surface flaws, whereas internal failures are caused by pores, facets, and inclusions. The three‐dimensional observation shows that fracture surfaces exhibit an irregular texture due to crystallographic mismatch of grains and plastic deformation at the crack tip. Based on EBSD analysis, Euler angles exhibited a complex geometry of grain orientation at the crack tip area, hindering crack propagation as evidenced by lower values of the Schmid factor and misorientation at the crack tip. Furthermore, the threshold values of small and long cracks decrease, whereas the transformation sizes from small to long crack growth increase from surface to internal failure. Finally, a novel microstructure defect‐based life prediction model is established, and the predicted results demonstrate a close resemblance to experimental outcomes.

materials science, multidisciplinary,engineering, mechanical
Effects of Heat Treatment on Microstructure and Low Cycle Fatigue Life of GH4169 Alloy

Xu ZENG,Xian-cheng ZHANG,Shan-tung TU,Fu-zhen XUAN

DOI: https://doi.org/10.11973/jxgccl201604006

2016-01-01

Abstract:The GH4169 alloy was treated using three heat treatment processes and the corresponding microstructures and the low cycle fatigue properties at the strain amplitude of 1.0%,0.8% and 0.5% at room temperature were studied.The results show that theδphase was precipitated in the microstructure of GH4169 alloy after the three heat treatments.The grain sizes before and after heat treatment had little difference.When adding a 900 ℃ solution treatment between solution and two-step aging treatments,the amount ofδphase precipitation in the alloy increased and moreδphases were obtained with longer holding time.Theδphase amounts almost had no influences on the fatigue lives of the GH4169 alloy.And the fatigue fracture surface at the same strain amplitude exhibited similar morphology.The number of crack sources increased with the increase of strain amplitude.
Very high cycle fatigue of a nickel-based superalloy at room and elevated temperatures: Interior failure behavior and life prediction

Xiaolong Li,Yucheng Zhang,Wei Li,Siqi Zhou,Rui Sun,Cheng Li,Ping Wang,Tatsuo Sakai

DOI: https://doi.org/10.1016/j.ijfatigue.2021.106349

IF: 5.489

2021-10-01

International Journal of Fatigue

Abstract:<p>Asymmetric load tests at 25 °C & 750 °C were performed to clarify the high-cycle-fatigue and very-high-cycle-fatigue properties of a nickel-based superalloy at elevated temperature. The life at 750 °C is longer due to the interior failure with crystallographic facets. Moreover, due to the competition between temperature and vacuum effects, threshold values for small and long cracks, as well as the transition crack size, are all lower at elevated temperature. Finally, based on proposed crack nucleation life model, fatigue life is evaluated by using fatigue-index-parameter, and predicted results are within a factor of three with respect to experimental data.</p>

materials science, multidisciplinary,engineering, mechanical
High Temperature Low-Cycle Fatigue, Deformation Microstructure and Final Fracture Behavior of a Nickel-Base Superalloy

Du Yi Ye,Jin Yang Zheng

DOI: https://doi.org/10.4028/www.scientific.net/kem.378-379.249

2008-01-01

Key Engineering Materials

Abstract:The low-cycle fatigue (LCF) properties of a nickel-base precipitation-strengthened superalloy (GH4145/SQ), obtained at a temperature of 538 o C, were reported and discussed in this paper. The properties investigated include cyclic stress response, fatigue life, deformation microstructure and final fracture features as a function of applied strain amplitude. It was shown that the alloy exhibited a pronounced initial hardening followed by continuous softening to failure at high plastic strain amplitudes ( > 0.2% ap ε ), while at low plastic strain amplitudes ( < 0.2% ap ε ) the initial hardening was followed by a well-defined saturation stage. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2% was observed in the cyclic stress-strain (CSS) and Coffin-Manson (C-M) plots. TEM observations revealed that slip band density increased with increasing total strain amplitude and precipitate degradation resulting from dislocation-precipitate interactions took place with continuous cyclic straining. The change in the microstructure during cycling is thus responsible for the fatigue hardening / softening behavior of the alloy. SEM examinations indicated that at low plastic strain amplitudes ( < 0.2% ap ε ) crack propagation was basically transgranular, while at high plastic strain amplitudes ( > 0.2% ap ε ) crack propagation exhibited intergranular features, as a whole. The variation in both the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain the observed two-stage LCF behavior of the present investigated superalloy.
Thermal fatigue crack initiation and propagation behaviors of GH3230 nickel‐based superalloy

Yujie Zhang,Cheng Hou,Xiaochao Jin,Dongxu Li,Litao Zhao,Laixia Yang,Xueling Fan

DOI: https://doi.org/10.1111/ffe.14168

IF: 3.373

2023-10-10

Fatigue & Fracture of Engineering Materials & Structures

Abstract:Abstract The drastic severe temperature cycle in an aero‐engine combustion chamber leads to large thermal fatigue stress, which may induce thermal fatigue failure of the combustion chamber. In this paper, thermal fatigue crack initiation and propagation behaviors of GH3230 nickel‐based superalloy sheet specimens with V‐notch were studied under different peak temperatures 800°C, 900°C, and 1,000°C using self‐built thermal fatigue equipment. The temperature, stress, and crack propagation driving force of the V‐notch specimen were discussed in detail. Results show that the thermal fatigue crack initiation life gradually decreases with the increase of the peak temperature. Oxidation caused by high temperature will weaken alloy's strength and accelerate its crack propagation. Higher peak temperature will make the crack propagate faster and the thermal deformation at V‐notch end easier to accumulate. At last, there is a good consistency between fitting curves from the modified Paris formula and the experiment results.

materials science, multidisciplinary,engineering, mechanical
High Temperature Fatigue and Creep-Fatigue Behaviors in a Ni-based Superalloy: Damage Mechanisms and Life Assessment

Run-Zi Wang,Shun-Peng Zhu,Ji Wang,Xian-Cheng Zhang,Shan-Tung Tu,Cheng-Cheng Zhang

DOI: https://doi.org/10.1016/j.ijfatigue.2018.05.008

IF: 5.489

2019-01-01

International Journal of Fatigue

Abstract:The low cycle fatigue (LCF) and creep-fatigue behaviors of Ni-based GH4169 superalloy are investigated by uniaxial strain-controlled fully-reversed testing at 650 degrees C. Compared with LCF tests, the effects of tensile and compressive strain hold times on creep-fatigue lifetimes are experimentally explored with varying total strain ranges in the present work. In order to elucidate the damage mechanisms under complex loading waveforms, an additional series of tests with both tensile and compressive hold times are carried out at a given total strain range of 2.0%. Posterior to the cyclic tests, main-crack-failure modes and secondary cracking modes are studied via optical microscopy (OM), scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD) techniques. Main-crack failure mechanisms are examined by the fracture appearance observations. Cracking modes are explored through quantitative characterization on the distributions of secondary cracks in the longitudinal cross sections under different loading waveforms. Moreover, a generalized life model based on linear damage summation (LDS) framework and energy dissipation criterion (EDC) is elaborated to estimate the damage mechanisms of fatigue, creep and oxidation. The prediction results can well establish the correlations between the reductions of numbers of cycles to failure and the presences of different damage mechanisms under respective loading waveforms.
A combined cyclic viscoplasticity and entropy generation approach for modelling fatigue crack growth behavior of nickel-based superalloy at high temperature

Shuyang Xia,Shuiting Ding,Zhenlei Li,Guo Li,Shaochen Bao,Bolin Li

DOI: https://doi.org/10.1016/j.engfracmech.2024.110032

IF: 5.4

2024-03-23

Engineering Fracture Mechanics

Abstract:This paper developed an entropy-based approach to estimate the fatigue crack growth (FCG) behavior of GH4169 at high temperature. Firstly, systematic FCG experiments of GH4169 at 650 °C were conducted to obtain the experimental data. Then, a finite element analysis combined with Chaboche viscoplasticity and node release technology was developed to obtain cyclic stress–strain responses and entropy generation fields. Based on thermodynamic analysis, numerous discrete material elements as sub-systems were divided along the crack growth direction in simplified representative 2D middle section. Fracture process zone (FPZ) was defined equal to the size of discrete material elements ( ρ ) which can be determined by distribution of normal stress perpendicular to the crack plane. Subsequently, an effective cyclic entropy generation related to ρ was defined as the crack driving force. Effective cumulative entropy generation was calculated when crack increment was ρ and the results indicated that effective cumulative entropy generation floating within a certain range. The average of all effective cumulative entropy generation values was defined as crack growth entropy. Finally, an entropy-based FCG rate model was established to estimate the FCG behavior of GH4169, and a good correlation between experimental results and model predictions are achieved for all the high temperature FCG tests.

mechanics
Very-High-Cycle Fatigue Behavior of Inconel 718 Alloy Fabricated by Selective Laser Melting at Elevated Temperature

Zongxian Song,Wenbin Gao,Dongpo Wang,Zhisheng Wu,Meifang Yan,Liye Huang,Xueli Zhang

DOI: https://doi.org/10.3390/ma14041001

IF: 3.4

2021-02-20

Materials

Abstract:This study investigates the very-high-cycle fatigue (VHCF) behavior at elevated temperature (650 °C) of the Inconel 718 alloy fabricated by selective laser melting (SLM). The results are compared with those of the wrought alloy. Large columnar grain with a cellular structure in the grain interior and Laves/δ phases precipitated along the grain boundaries were exhibited in the SLM alloy, while fine equiaxed grains were present in the wrought alloy. The elevated temperature had a minor effect on the fatigue resistance in the regime below 108 cycles for the SLM alloy but significantly reduced the fatigue strength in the VHCF regime above 108 cycles. Both the SLM and wrought specimens exhibited similar fatigue resistance in the fatigue life regime of fewer than 107–108 cycles at elevated temperature, and the surface initiation mechanism was dominant in both alloys. In a VHCF regime above 107–108 cycles at elevated temperature, the wrought material exhibited slightly better fatigue resistance than the SLM alloy. All fatigue cracks are initiated from the internal defects or the microstructure discontinuities. The precipitation of Laves and δ phases is examined after fatigue tests at high temperatures, and the effect of microstructure on the formation and the propagation of the microstructural small cracks is also discussed.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
High‐cycle and very‐high‐cycle fatigue behavior and life prediction of Ni‐based superalloy at elevated temperature

Xiaolong Li,Yucheng Zhang,Wei Li,Siqi Zhou,Ping Wang

DOI: https://doi.org/10.1111/ffe.13573

2021-09-14

Abstract:The tension–tension test with stress ratio 0.1 was conducted to clarify high-cycle and very-high-cycle fatigue properties of Ni-based superalloy at 750°C by combining two- and three-dimensional microscopic observations. Results show that as stress level decreases, fatigue failure is less likely to be induced by pore, while the possibility of crystallographic facet-induced failure increases, and finally, the duplex S–N curves are formed. The larger roughness of crack nucleation region is mainly attributed to the geometric incompatibility of grains and the plastic deformation at crack tip. Under the influence of elevated temperature and vacuum environment, the transition size from small crack to long crack is approximately equal to the grain size. Combined with the evaluation of threshold values, the internal failure mechanism is elucidated. Finally, from the viewpoint of energy, a fatigue life prediction model is proposed, and the predicted results are in good agreement with the experimental ones.

materials science, multidisciplinary,engineering, mechanical

Very high cycle fatigue behaviors of GH4169 superalloy at room and high temperatures

Effect of Initial Overload on the Low Cycle Fatigue Life of Gh4169 Alloy at Different Temperatures

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

High-temperature Oxidation Behavior of AlCoCrCuFeNi High-Entropy Alloy by Selective Laser Melting

High-Temperature Low-Cycle Fatigue Properties of GH4169 Ni-based Superalloy

Crack initiation mechanisms and life prediction of GH4169 superalloy in the high cycle and very high cycle fatigue regime

Interior long‐life‐fatigue cracking behavior and life prediction of a selective laser melted GH4169 superalloy at different temperatures and stress ratios

High Temperature Low Cycle Fatigue Behavior of GH4742 Alloy

Microstructures' Effects on High Temperature Fatigue Failure Behavior of Typical Superalloys

Combined high and low cycle fatigue analysis of FGH96 alloy under high temperature conditions

Competitive Fracture Mechanism and Microstructure‐Related Life Assessment of GH4169 Superalloy in High and Very High Cycle Fatigue Regimes

Effects of Heat Treatment on Microstructure and Low Cycle Fatigue Life of GH4169 Alloy

Very high cycle fatigue of a nickel-based superalloy at room and elevated temperatures: Interior failure behavior and life prediction

High Temperature Low-Cycle Fatigue, Deformation Microstructure and Final Fracture Behavior of a Nickel-Base Superalloy

Thermal fatigue crack initiation and propagation behaviors of GH3230 nickel‐based superalloy

High Temperature Fatigue and Creep-Fatigue Behaviors in a Ni-based Superalloy: Damage Mechanisms and Life Assessment

A combined cyclic viscoplasticity and entropy generation approach for modelling fatigue crack growth behavior of nickel-based superalloy at high temperature

Very-High-Cycle Fatigue Behavior of Inconel 718 Alloy Fabricated by Selective Laser Melting at Elevated Temperature

High‐cycle and very‐high‐cycle fatigue behavior and life prediction of Ni‐based superalloy at elevated temperature