Room‐temperature multiferroic characteristics and unique vortex domain structures of h ‐Yb 1− x In x FeO 3 solid solutions

Mei Ying Liu,Tu Lai Sun,Xiao Li Zhu,Xiao Qiang Liu,He Tian,Xiang Ming Chen

DOI: https://doi.org/10.1111/jace.17987

IF: 4.186

2021-07-09

Journal of the American Ceramic Society

Abstract:<p>Hexagonal rare earth ferrites (<i>h</i>-RFeO₃) have attracted much scientific attention due to their room-temperature multiferroicity. However, it is still a hard job to obtain <i>h</i>-RFeO₃ bulk materials because of the meta-stability of such hexagonal phase, and the evaluation of room-temperature ferroelectric and magnetoelectric characteristics in such materials is also a challengeable issue. In the present work, Yb_1-xIn_xFeO₃ ceramics with stable hexagonal structure were obtained by introducing chemical pressure, where the unique ferroelectric domain structures of sixfold vortex combined with tenfold vortex with a typical size of ~400 nm were determined. Symmetry of the present system evolved from centrosymmetric orthorhombic <i>Pbnm</i> (x=0-0.4) to non-centrosymmetric hexagonal <i>P6₃cm</i> (x=0.5&amp;0.6) with the ferroelectric polarization up to 3.2 μC/cm², and finally to centrosymmetric hexagonal <i>P6₃/mmc</i> (x=0.7&amp;0.8). The Curie point decreased monotonically from 723 K to a temperature below room temperature with increasing x, and the antiferromagnetic phase transition above room temperature was determined for all compositions. Meanwhile, a large linear magnetoelectric coefficient (<i>α_ME</i>) up to 0.96 mV/cm Oe was obtained at room temperature, and this indicated the great application potential for magnetoelectric devices.</p>

materials science, ceramics