Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

A Mg-6Y-3Zn-1Al Mg HPDC alloy having high thermal stability: Study of grain growth kinetics

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Exceptional thermal stability and enhanced hardness in a nanostructured Mg-Gd-Y-Zn-Zr alloy processed by high pressure torsion

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

High-Temperature Stability of Mg–1Al–12Y Alloy Containing LPSO Phase and Mechanism of Its Portevin–Le Chatelier (PLC) Effect

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

The Aging Behaviour of a Mg-10Gd-3Y-1.0Zn-0.5Zr (wt.%) Alloy with Long-Period Stacking Ordered Phase at 275°C

A novel die-casting Mg alloy with superior performance: Study of microstructure and mechanical behavior

The Microstructural Evolution and Grain Growth Kinetics of Fine-Grained Extruded Mg-Nd-Zn-Zr Alloy

Precipitate evolution of as-cast Mg-9Gd-2Y-0.5Zn-0.5Zr alloy containing LPSO, β′′, β′ and γ'' phases during isothermal aging at 200 °C

Dynamic nano precipitation behavior of as-cast Mg-4Li-4Zn-Y alloy during high temperature deformation

A high performance Mg-Al-Ca alloy processed by high pressure die casting: Microstructure, mechanical properties and thermal conductivity

High Strength Extruded Mg–5Zn–2Nd–1.5Y–0.6Zr–0.4Ca Alloy Produced by Electromagnetic Casting

Realizing impressive superplasticity in a low-alloyed Mg-Zn-Ca-Al-Mn alloy: The roles of grain boundary segregation and dense β-Mn particles

Deformation behaviors and the related high-temperature mechanical properties of Mg-11Gd-5Y-2Zn-0.7Zr via regulating extrusion temperatures

Microstructure and thermal stability of nanocrystalline Mg-Gd-Y-Zr alloy processed by high pressure torsion

The Effect of Morphology of the Long-Period Stacking Ordered Phase on Mechanical Properties of the Mg-7Gd-3Y-1Nd-1Zn-0.5Zr (wt.%) Alloy

Effects of heat treatment on mechanical properties of an extruded Mg-4.3Gd-3.2Y-1.2Zn-0.5Zr alloy and establishment of its Hall–Petch relation

Effect of Annealing on Microstructure and Tensile Properties of As-Extruded Mg-5Gd-4Y-0.5Zn-0.5Zr Alloy

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Microstructure Evolution and Mechanical Properties of Mg-7Gd-3Y-1Nd-2Zn-0.5Zr Alloy During Two-Step Homogenization Heat Treatment