Abstract:The microstructure evolution and mechanical properties of Al–3.92Cu–1.10Li–0.68Mg–0.32Ag–0.23Mn–0.35Zn–0.11Zr and Al–3.92Cu–1.12Li–0.76Mg–0.29Ag–0.24Mn–0.24Zn–0.12Zr–0.083Sc (wt%) alloys during homogenization with different cooling modes were comprehensively studied. It was clearly revealed that the minor Sc addition refined the grains of as-cast Al–Cu–Li–Mg alloys through the formation of primary Al3(Sc, Zr) phases during the solidification process, and induced Sc enrichment in the θ (Al2Cu) eutectic. After the homogenization treatment, the majority of coarse nonequilibrium eutectic phases at the grain boundaries dissolved into the α-Al matrix, leading to the relatively uniform distribution of each element. Sc-added alloy after homogenization treatments possessed more superior strength and ductility than Sc-free alloy. Compared to the furnace cooling mode, the air cooling mode could inhibit the precipitation of micron-sized coarse T1 (Al2CuLi) phase and improve the mechanical properties of the alloys. After homogenization, the continuous Al2Cu phase in the as-cast Sc-added alloy dissolved and transformed to an array of W-(Al, Cu, Sc) ternary phase, which was identified as Al6Cu6Sc with the body-centered tetragonal structure. The appearance of spherical Al6Cu6Sc particle could not damage the mechanical properties of Al–Cu–Li–Mg alloys after the homogenization treatment. The tensile strength, yield strength and elongation of Sc-added alloy after the homogenization by air cooling were 390 MPa, 265 MPa and 10.8%, respectively. The investigation of Al6Cu6Sc phase offered a potential avenue to produce high-quality Sc-added 2xxx series alloys.Graphic

Quench sensitivity and microstructures of high-Zn-content Al−Zn−Mg−Cu alloys with different Cu contents and Sc addition

Effects of Sc and Zr microalloying on the microstructure and mechanical properties of high Cu content 7xxx Al alloy

Influence of Mg Content on Quench Sensitivity of Al–Zn–Mg–Cu Aluminum Alloys

Study on quenching sensitivity of an Al–Zn–Mg–Cu alloy containing trace amounts of Sc and Zr

Quench sensitivity and microstructure evolution of the 2060 Al-Cu-Li alloy with a low Mg content

The Effect of Cu and Sc on the Localized Corrosion Resistance of Al-Zn-Mg-X Alloys

Microstructure, Mechanical Properties and Corrosion Behaviors of Al–Li–Cu–Mg–Ag–Zn Alloys

Quench rate sensitivity of age-hardenable Al-Zn-Mg-Cu alloys with respect to the Zn/Mg ratio: An in situ SAXS and HEXRD study

Microstructure evolution and quench sensitivity characterizations of Mg-9.5Gd-0.9Zn-0.5Zr alloy

Role of Cu on the Mechanical Properties and Microstructures Evolution of Al-xCu-1Li-0.4Mg–1Zn-0.1Zr Alloys

Influence of Cu content on the hardenability of Al-xCu-1.1Li alloys

Influence of Sc Content on the Microstructure and Mechanical Properties of Cast Al-2Li-2Cu-0.5Mg-0.2Zr Alloy

Effect of Cu Additions on Microstructure, Mechanical Properties and Hot-Tearing Susceptibility of Mg-6Zn-0.6Zr Alloys

The microstructures and mechanical properties of a highly alloyed Al-Zn-Mg-Cu alloy: The role of Cu concentration

Influence of Sc and Zr additions on microstructure and properties evolution of Al–Zn–Mg alloy

Influences of Mg content on the microstructures and mechanical properties of cast Al–2Li–2Cu–0.2Zr alloy

Microstructural characteristics and mechanical properties of cast Al-3Li-xCu-0.2Zr alloy

Effect of Minor Sc Addition on the Microstructure Evolution of Al–Cu–Li–Mg Alloy During Homogenization with Different Cooling Modes

Study on the effect of enhanced magnesium and copper contents on microstructure and property of Al-Zn-Mg-Cu alloys with high zinc element content during fabrication processes

Effect of Quenching Rate on Microstructure, Mechanical and Corrosion Properties of Al-Zn-Mg-Cu-Cr-Zr Alloy

Influence of Sc Addition on Precipitation Behavior and Properties of Al-Cu-Mg Alloy