Abstract:Abstract Recently, flat panel display technologies are based on amorphous silicon (a-Si), polycrystalline silicon (poly-Si) or amorphous oxide semiconductor (AOS) thin film transistors (TFTs) technology. In order to reach higher performance for ultra-high resolution display applications, the material selection for the channel layer is vital. AOS TFTs drawn lots of attention because of its advantages such as low leakage current, high driving current and high uniformity [1,3]. In this work, we presented a novel amorphous oxide semiconductor (AOS) material of gallium-free a-InWZnO thin film transistors (IWZO TFTs) which is very promising to be applied for ultra-high resolution display technology. Experiment In this work, we demonstrated the structure of a-IWZO TFTs processes. Figure 1 shows the schematic of the TFT cross-section. After growing a 550 nm thermal oxide layer as buffer layer, a 25-nm-thick of molybdenum was deposited by DC-sputter as the bottom gate electrode. A 10-nm-HfO 2 was deposited by plasma-enhanced atomic layer deposition (PEALD) system as high-κ gate dielectric (GI). Then, post deposition annealing (PDA) was carried out to enhance the quality of the insulator layer. Next, an ultra-thin body a-IWZO was deposited by RF-sputter as channel layer. Finally, source and drain were defined by lift-off process and the gate contact via was etched by dry etching to finish the device fabrication. Result and Discussion Figure 1(b) shows the negative gate bias stress (NGBS) transfer curve (I D -V G ) of a-IWZO TFTs with passivation layer. The experimental results have shown that passivation layer could keep the back channel of IWZO channel from exposing to oxygen and hydrogen from the atmosphere. Without the passivation layer, the back channel would contact moisture leading the diffused hydrogen atoms to fill oxygen vacancy sites and de-trap free carriers, causing the V TH shifts negatively. The ultra-thin a-IWZO TFTs with passivation layer exhibited a low subthreshold swing (S.S.) of 89.7 mV/dec, high on/off current ratio (I ON /I OFF ) of 2.1×10 7 and small threshold voltage shift (ΔV th ) of -0.097 V during NGBS of -2MV/cm with 2000s. To sum up, the passivation layer could enhance the a-IWZO TFTs reliability. Reference [1] Kamiya, H. Hosono, NPG Asia Mater ., vol. 2, pp. 15, 2010. [2] Nomura, H. Ohta, A. Takagi, T. Kamiya, M. Hirano, and H. Hosono, nature, vol. 432, no. 7016, pp. 488-492, 2004. [3] Y. Kuo, C. M. Chang, I. H. Liu, and P. T. Liu, Scientific reports, vol. 9, no. 1, pp. 1-7, 2019. Figure 1

High-mobility and high-reliability Zn-incorporated amorphous In2O3-based thin-film transistors

Fully solution-induced high performance indium oxide thin film transistors with ZrOx high-k gate dielectrics

Reliable operation in high-mobility indium oxide thin film transistors

Fabrication and performance of indium oxide based transparent thin film transistors

High Reliability Tungsten-Doped Indium Zinc Oxide Thin Film Transistors for Display Applications

Effect of Indium Doping on Bias Stability in Dual-Target Co-Sputtering InZnSnO Thin-Film Transistors

Nitrogen-Doped Amorphous InZnSnO Thin Film Transistors with a Tandem Structure for High-Mobility and Reliable Operations

Combustion-Process Derived Comparable Performances of Zn-(In:Sn)-O Thin-Film Transistors with A Complete Miscibility

Exploring the Potential of InCp Precursor in Plasma-Enhanced Atomic Layer Deposition for High-Performance IZO-TFTs

High-Performance Amorphous InGaZnO Thin Film Transistor With High-k Van Der Waals Molecular Dielectric

High‐Performance Thin‐Film Transistors with Nickel‐Doped Indium Zinc Oxide Channel Layers

Remarkable Bias‐Stress Stability of Ultrathin Atomic‐Layer‐Deposited Indium Oxide Thin‐Film Transistors Enabled by Plasma Fluorination

High-Performance of InGaZnO TFTs With an Ultrathin 5-nm Al2O3 Gate Dielectric Enabled by a Novel Atomic Layer Deposition Method

Back-End-of-Line Compatible InSnO/ZnO Heterojunction Thin-Film Transistors With High Mobility and Excellent Stability

High-Performance of InGaZnO TFTs With an Ultrathin 5-nm Al<sub>2</sub>O<sub>3</sub> Gate Dielectric Enabled by a Novel Atomic Layer Deposition Method

High-Performance of InGaZnO TFTs With an Ultrathin 5-nm Al₂O₃ Gate Dielectric Enabled by a Novel Atomic Layer Deposition Method

Feasibility of Atomic Layer Deposited AlZrOx Film to Achieve High Performance and Good Stability of ZnSnO-TFT

Effect of HfO2-Based Multi-Dielectrics on Electrical Properties of Amorphous In-Ga-Zn-O Thin Film Transistors

Electrical Properties of Amorphous Indium Zinc Tin Oxide Thin Film Transistor with Y₂O₃ Gate Dielectric

Enhancing Reliability of Short-channel Dual gate InGaZnO Thin Film Transistors by Bottom-gate Oxide Engineering

Aggressively Scaled Atomic Layer Deposited Amorphous InZnOx Thin Film Transistor Exhibiting Prominent Short Channel Characteristics (SS= 69 mV/dec.; DIBL = 27.8 mV/V) and High Gm(802 μS/μm at VDS = 2V)