Abstract:Composites that use fly ash and slag as alkali-activated materials instead of cement can overcome the defects and negative effects of alkali-activated cementitious materials prepared with the use of an alkali-activated material. In this study, fly ash and slag were used as raw materials to prepare alkali-activated composite cementitious materials. Experimental studies were carried out on the effects of the slag content, activator concentration and curing age on the compressive strength of the composite cementitious materials. The microstructure was characterized using hydration heat, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), mercury intrusion porosimetry (MIP) and scanning electron microscopy (SEM), and its intrinsic influence mechanism was revealed. The results show that increasing the curing age improves the degree of polymerization reaction and the composite reaches 77~86% of its 7-day compressive strength after 3 days. Except for the composites with 10% and 30% slag content, which reach 33% and 64%, respectively, of their 28-day compressive strength at 7 days, the remaining composites reach more than 95%. This result indicates that the alkali-activated fly ash–slag composite cementitious material has a rapid hydration reaction in the early stage and a slow hydration reaction in the later stage. The amount of slag is the main influencing factor of the compressive strength of alkali-activated cementitious materials. The compressive strength shows a trend of continuous increase when increasing slag content from 10% to 90%, and the maximum compressive strength reaches 80.26 MPa. The increase in the slag content introduces more Ca2+ into the system, which increases the hydration reaction rate, promotes the formation of more hydration products, refines the pore size distribution of the structure, reduces the porosity, and forms a denser microstructure. Therefore, it improves the mechanical properties of the cementitious material. The compressive strength shows a trend of first increasing and then decreasing when the activator concentration increases from 0.20 to 0.40, and the maximum compressive strength is 61.68 MPa (obtained at 0.30). The increase in the activator concentration improves the alkaline environment of the solution, optimizes the level of the hydration reaction, promotes the formation of more hydration products, and makes the microstructure denser. However, an activator concentration that is too large or too small hinders the hydration reaction and affects the strength development of the cementitious material.

Alkali-activated slag mortar molded by non-stirring molding: Compressive strength, hydration properties and microstructures

Microstructure, strength development mechanism, and CO2 emission analyses of alkali-activated fly ash-slag mortars

Mechanical Performance and Durability of Mortar Based on Slag Cement and NaOH-Activated Slag

Effect of borax-modified activator on mechanical properties and drying shrinkage of alkali-activated slag/metakaolin mortar

Recent progress in understanding setting and hardening of alkali-activated slag (AAS) materials

Effects of Mud Content on the Setting Time and Mechanical Properties of Alkali-Activated Slag Mortar

Performance Enhancement of Alkali-Activated Electric Arc Furnace Slag Mortars through an Accelerated CO2 Curing Process

A novel admixture to improve durability of alkali-activated slag by reducing water sorptivity and optimising the process of activation

Microstructures and properties of alkali-activated slags with composite activator: Effects of Na2O equivalents

Effect of Steel Slag on the Properties of Alkali-Activated Slag Material: A Comparative Study with Fly Ash

New Insights into Pore Structure and Hydraulic Conductivity of Sodium Hydroxide Alkali-Activated Slag through Advanced Modelling

Properties of Alkali-Activated Slag Cement Activated by Weakly Alkaline Activator

Rheology and alkali-silica reaction of alkali-activated slag mortars modified by fly ash microsphere: a comparative analysis to OPC mortars

Approaches to enhance the carbonation resistance of fly ash and slag based alkali-activated mortar- experimental evaluations

Properties, Microstructure Development and Life Cycle Assessment of Alkali-Activated Materials Containing Steel Slag under Different Alkali Equivalents

Recent Advances In Chemical Admixtures For Improving The Workability Of Alkali-Activated Slag-Based Material Systems

Factors Affecting Kinetics and Gel Composition of Alkali–Silica Reaction in Alkali-Activated Slag Mortars

Study of the Mechanical Properties and Microstructure of Alkali-Activated Fly Ash–Slag Composite Cementitious Materials

Effect of Alkaline-Earth Metal Oxide on Compressive Strength and Flexural Strength of Alkali-Activated Slag Cement Mortar

Fluidity, mechanical properties, shrinkage of alkali-activated slag/stainless steel slag mortars with composite activators

Properties of Alkli-Activated Slag Cement Compounded with Soluble Glasses with A High Silicate Modulus