Abstract:Composites that use fly ash and slag as alkali-activated materials instead of cement can overcome the defects and negative effects of alkali-activated cementitious materials prepared with the use of an alkali-activated material. In this study, fly ash and slag were used as raw materials to prepare alkali-activated composite cementitious materials. Experimental studies were carried out on the effects of the slag content, activator concentration and curing age on the compressive strength of the composite cementitious materials. The microstructure was characterized using hydration heat, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), mercury intrusion porosimetry (MIP) and scanning electron microscopy (SEM), and its intrinsic influence mechanism was revealed. The results show that increasing the curing age improves the degree of polymerization reaction and the composite reaches 77~86% of its 7-day compressive strength after 3 days. Except for the composites with 10% and 30% slag content, which reach 33% and 64%, respectively, of their 28-day compressive strength at 7 days, the remaining composites reach more than 95%. This result indicates that the alkali-activated fly ash–slag composite cementitious material has a rapid hydration reaction in the early stage and a slow hydration reaction in the later stage. The amount of slag is the main influencing factor of the compressive strength of alkali-activated cementitious materials. The compressive strength shows a trend of continuous increase when increasing slag content from 10% to 90%, and the maximum compressive strength reaches 80.26 MPa. The increase in the slag content introduces more Ca2+ into the system, which increases the hydration reaction rate, promotes the formation of more hydration products, refines the pore size distribution of the structure, reduces the porosity, and forms a denser microstructure. Therefore, it improves the mechanical properties of the cementitious material. The compressive strength shows a trend of first increasing and then decreasing when the activator concentration increases from 0.20 to 0.40, and the maximum compressive strength is 61.68 MPa (obtained at 0.30). The increase in the activator concentration improves the alkaline environment of the solution, optimizes the level of the hydration reaction, promotes the formation of more hydration products, and makes the microstructure denser. However, an activator concentration that is too large or too small hinders the hydration reaction and affects the strength development of the cementitious material.

Microstructure, strength development mechanism, and CO2 emission analyses of alkali-activated fly ash-slag mortars

Alkali-activated slag & fly ash as sustainable alternatives to OPC: Sorptivity and strength development characteristics of mortar

Low carbon cementitious materials: Sodium sulfate activated ultra-fine slag/fly ash blends at ambient temperature

Rheology and alkali-silica reaction of alkali-activated slag mortars modified by fly ash microsphere: a comparative analysis to OPC mortars

Effect of Steel Slag on the Properties of Alkali-Activated Slag Material: A Comparative Study with Fly Ash

Design and Microstructural Analysis of the Mixture Proportion of Alkali-Activated Fly Ash-Slag Composite Cementitious Material

Study of the Mechanical Properties and Microstructure of Alkali-Activated Fly Ash–Slag Composite Cementitious Materials

Effect of CaO on the shrinkage and microstructure of alkali-activated slag/fly ash microsphere

Microstructures and properties of alkali-activated slags with composite activator: Effects of Na2O equivalents

Assessment of the performance of alkali-activated slag/fly ash using liquid and solid activators: early-age properties and efflorescence

Approaches to enhance the carbonation resistance of fly ash and slag based alkali-activated mortar- experimental evaluations

The Effect of Blast Furnace Slag/Fly Ash Ratio on Setting, Strength, and Shrinkage of Alkali-Activated Pastes and Concretes

Chloride Ions' Penetration of Fly Ash and Ground Granulated Blast Furnace Slags-Based Alkali-Activated Mortars

Microstructure and macro properties of sustainable alkali-activated fly ash mortar with various construction waste fines as binder replacement up to 100%

Effect of fly ash and gypsum on drying shrinkage and mechanical properties of one‐part alkali‐activated slag mortar

Experimental study on full-volume slag alkali-activated mortars: Air-cooled blast furnace slag versus machine-made sand as fine aggregates

Factors affecting compressive strength and expansion due to alkali-silica reaction of fly ash-based alkaline activated mortar

Alkali-activated slag mortar molded by non-stirring molding: Compressive strength, hydration properties and microstructures

Strength and Microstructural Characteristics of Activated Fly Ash–Cement Paste

Properties, Microstructure Development and Life Cycle Assessment of Alkali-Activated Materials Containing Steel Slag under Different Alkali Equivalents

Effect of Activator and Mineral Admixtures on the Autogenous Shrinkage of Alkali-Activated Slag/Fly Ash