Abstract:Research on water quenched silicomanganese slag (WQSMS) has primarily focused on grinding it into micro-powder to be used as auxiliary cementitious materials or to synthesize alkali-activated cementitious materials. However, there is a lack of research on utilizing WQSMS as fine aggregates instead of natural aggregates. Although its properties are similar to granulated blast furnace slag (GBFS), most studies investigating the use of GBFS as fine aggregates have mainly focused on mechanical properties rather than microstructure analyses. Meanwhile, to make full use of industrial solid waste, reduce CO2 emissions, and save energy consumption, solid waste cementitious material based on steel slag (SS), desulphurized gypsum (DG), and GBFS, as well as WQSMS as fine aggregate to replace ISO standard sand and washed-out sand (WOS) in various proportions(0%, 25%, 50%, 75%, and 100%) to prepare mortar and concrete, respectively. Analyses of workability, mechanical properties, and microstructure were carried out, and the improvement of mechanical properties of WQSMS was analyzed by SEM-EDS, SEM-BSE, and the microhardness test. The results show that with the increase of WQSMS, the workability of mortar and concrete decreased, while the mechanical strength increased first and then decreased. The mechanical strengths of them reached the peak when the WQSMS addition reached 50%. The flexural and compressive strengths of the mortar increased by 40% and 9.7%, respectively, while the tensile splitting strength and compressive strength of the concrete increased by 11.9% and 3.4%, respectively. The microstructure of the interfacial transition zone(ITZ) was greatly enhanced by WQSMS, which decreased the porosity by 10.49%, decreased the thickness by 27.27%, and increased the microhardness by 11.0%. However, when the content surpasses 50%, the mechanical strength of mortar and concrete declined due to the loose porosity and poor mechanical strength of WQSMS, and there was insufficient cementitious material to fill these holes. Nonetheless, with 100% content, the mortar maintained its high-performance status, with a flexural strength of 8.0 MPa and a compressive strength of 47.9 MPa, and the concrete still fulfilled the specifications of regular concrete C40. Both the fine aggregate and the cementitious material were composed of solid waste, showing potential environmental benefits and interesting green products for future studies.

Experimental study on full-volume slag alkali-activated mortars: Air-cooled blast furnace slag versus machine-made sand as fine aggregates

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Admixture Effects on the Rheological/Mechanical Behavior and Micro-Structure Evolution of Alkali-Activated Slag Backfills

Study on the properties of alkali-activated phosphorus slag mortar mixed with granulated blast furnace slag/fly ash

Recycling air-cooled blast furnace slag in fiber reinforced alkali-activated mortar

Properties, Microstructure Development and Life Cycle Assessment of Alkali-Activated Materials Containing Steel Slag under Different Alkali Equivalents

Effect of water quenched silicomanganese slag as fine aggregate on mechanical properties and microstructure characteristics of solid waste-based mortar and concrete

Structure, morphology and compressive strength of Alkali-activated mortars containing waste bottle glass nanoparticles

Study on the preparation, performance, and mechanism for solid waste cementitious materials

Microstructure, strength development mechanism, and CO2 emission analyses of alkali-activated fly ash-slag mortars

Investigation on the properties of sustainable alkali-activated GGBS mortar with nano silica and dredged marine sand: Mechanical, microstructural and durability aspects

Utilization of ultra-fine dredged sand from the Yangtze River in alkali-activated slag/fly ash mortars: Mechanical properties, drying shrinkage and microstructure

Effects of Incineration Waste Ash and Gypsum Substitution on the Properties of Blast Furnace Slag Mortar using Recycled Aggregate

Effect of Waste Ceramic Powder on Properties of Alkali-Activated Blast Furnace Slag Paste and Mortar

Modification mechanism of flue gas desulfurization gypsum on fly ash and ground granulated blast-furnace slag alkali-activated materials: Promoting green cementitious material

Microstructure and macro properties of sustainable alkali-activated fly ash mortar with various construction waste fines as binder replacement up to 100%

The Multifaceted Comparison of Effects of Immobilisation of Waste Imperial Smelting Furnace (ISF) Slag in Calcium Sulfoaluminates (CSA) and a Geopolymer Binder

Evaluation of copper slag and stainless steel slag as replacements for blast furnace slag in binary and ternary alkali-activated cements

Microstructures and properties of alkali-activated slags with composite activator: Effects of Na2O equivalents

Rheology and alkali-silica reaction of alkali-activated slag mortars modified by fly ash microsphere: a comparative analysis to OPC mortars

Preparation and microstructure analysis of alkali-activated ground granulated blast furnace slag-steel slag grouting materials