The Multifaceted Comparison of Effects of Immobilisation of Waste Imperial Smelting Furnace (ISF) Slag in Calcium Sulfoaluminates (CSA) and a Geopolymer Binder

Beata Łaźniewska-Piekarczyk,Monika Czop,Jan Antoni Rubin

DOI: https://doi.org/10.3390/ma17133163

IF: 3.4

2024-06-28

Materials

Abstract:Using waste materials as replacements for sand in building materials helps reduce waste and improve the properties and sustainability of the construction materials. Authors proved the possibility of using imperial smelting furnace (ISF) slag granules as a 100% substitute for natural sand in self-compacting (SCC) cement-based mortars of calcium sulfoaluminates (CSA). The study proved that ISF slag's radioactive properties meet this area's requirements. CSA cement eliminates the noted problem in the case of concrete with Portland cement, which is the extended setting of the cement binder. The research findings indicate that using slag to replace sand up to 100% in mortars without grains smaller than 0.125 mm allows high flowability, compaction, low porosity and mechanical parameters. The compressive strength of the CSA cement mortars was about 110 MPa, and more than 140 MPa for geopolymer mortar. Unfortunately, the alkaline pH of a geopolymer causes high leachability of barium and sodium. Thus, the CSA cement is in a more favourable binder to achieve high strength, is environmentally friendly, and is a self-compacting mortar or concrete.

materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter

What problem does this paper attempt to address?

The paper mainly discusses the effect of using Imperial Smelting Furnace (ISF) slag as a substitute for natural sand in Calcium Sulfoaluminate (CSA) cement and a type of geopolymer binder. The author's research demonstrates that ISF slag can fully replace natural sand in self-compacting concrete (SCC) based on CSA cement, and its radioactivity meets the industry standards. CSA cement solves the issue of extended concrete curing time when using Portland cement. The study found that mortar with slag completely replacing sand has high fluidity, low porosity, and good mechanical properties. However, the high alkalinity of the geopolymer leads to high leaching of barium and sodium, making CSA cement more advantageous for achieving high strength, environmental-friendly, and self-compacting mortar or concrete.

The paper first introduces the background of using alternative aggregates in construction materials and highlights the importance of substitute aggregates in the construction industry due to limited resources and increased environmental awareness. Then, it analyzes in detail the chemical composition, physical properties, and influence of ISF slag on mortar performance. In the study, ISF slag prepared properly is used to produce SCC cement and geopolymer mortar, and various indicators such as fluidity, radioactivity, porosity, and mechanical properties are compared.

The experimental section describes in detail the characterization tests of ISF slag, the preparation methods of cement and geopolymer mortar, as well as the testing procedures for fresh and hardened mortar. The results show that ISF slag significantly improves the strength of mortar, with compressive strength of approximately 110 MPa for CSA cement mortar and over 140 MPa for geopolymer mortar. Additionally, the paper evaluates the fixation efficiency of ISF slag in cement and geopolymer mortar, and verifies its controllability on environmental impact through leaching tests according to the EN 12457-2 standard.

In conclusion, this paper aims to address the demand for sustainable aggregates in the construction industry and experimentally validates the suitability and superiority of ISF slag as a substitute for sand in SCC cement and geopolymer mortar. It provides a new solution for the recycling of industrial waste.