In Situ Thermal Interactions of Cu-Based Anti-Corrosion Coatings on Steel Implemented by Surface Alloying

Huda Hanif Khan,Tong Wang,Lihong Su,Huijun Li,Qiang Zhu,Ana Yang,Zigang Li,Wei Wang,Hongtao Zhu

DOI: https://doi.org/10.3390/coatings14060722

IF: 3.236

2024-06-06

Coatings

Abstract:Incorporating expensive alloying elements into bulk steel for corrosion protection is undesirable, considering that only the surfaces are exposed to aggressive environments. Therefore, this work focused on developing and optimizing a new surface functioning technology through in situ observation of thermal interactions between the metallic powders at elevated temperatures. The study revealed that the Cu-Ni powder mixture, with 12.5 wt% Ni, began to melt at 1099.5 °C and was fully melted at 1175 °C, significantly different from the Cu-Ni solid solution and bulk Cu or Ni. As a result of high-temperature reactions, copper penetration of up to 35 μm for pure copper and 55 μm for copper-chromium composite coatings occurred due to liquid metal corrosion. In contrast, the copper-nickel composite coating exhibited a cupronickel solution microstructure with FeNi dendrites and a nickel-rich transition layer. This cupronickel coating, with a chemical composition of 89.3 wt% Cu, 6.2 wt% Ni, and 4.5 wt% Fe, demonstrated uniform thickness, superior surface morphology, and continuous coverage on the steel substrate. Furthermore, the Ni-rich transition layer played a vital role in preventing copper penetration along the grain boundary of the steel matrix while forming a chemical binding between the coating and the substrate. The practicality of the coating was further confirmed through the hot-rolling procedure and subsequent electrochemical corrosion tests, which resulted in a 44% improvement in corrosion resistance.

materials science, multidisciplinary, coatings & films,physics, applied