Corrosion behavior and antifouling ability of Cu-Zn-Al/Zn-Al composite coating on Q235 steel

Yan Qi,Wenping Liang,Qiang Miao,Hao Lin,Hao An,Yangyang Liu,Shiwei Zuo,Hairui Ma

DOI: https://doi.org/10.1016/j.surfcoat.2020.126614

IF: 4.865

2021-01-01

Surface and Coatings Technology

Abstract:In this study, a Cu-Zn-Al/Zn-Al coating was prepared on Q235 steel by a dip-spin method and the corrosion behavior of the composite coating was also analyzed. The evolution of morphology and phase structure proved the corrosion products transited from the Zn-containing to Al-containing. The potential dynamic results manifested that the corrosion current density of the coated sample (1.42 × 10−6 A·cm2) is two orders of magnitude lower than the substrate. From the impendence plots, it can be found that the impendence resistance of the original Cu-Zn-Al/Zn-Al coating is up to 1.58 × 104 Ω·cm2 due to the existence of the silane and oxide film. With increasing exposure time of aggressive environment, the resistance decreased and then gradually rise to approximately 1.0 × 104 Ω·cm2. Besides, the results of the antifouling test showed the copper leaching remained at a stable value of about 20 μg·cm−2·d−1 which could inhibit most algae, eventually up to 95% lethal effect on N. closterium.

physics, applied,materials science, coatings & films

What problem does this paper attempt to address?

The paper attempts to address the issue of improving the corrosion resistance and antifouling capabilities of Q235 steel in marine environments. Specifically, the researchers prepared a Cu-Zn-Al/Zn-Al composite coating on the surface of Q235 steel using the dip-spin method and conducted a detailed study on its corrosion resistance behavior and antifouling performance. The main objectives of the paper include:

1. **Improving Corrosion Resistance**: By preparing a Cu-Zn-Al/Zn-Al composite coating on the surface of Q235 steel, the study investigates its corrosion behavior in a 3.5 wt.% NaCl solution to evaluate its corrosion resistance effect.

2. **Enhancing Antifouling Capability**: The study examines the release rate of copper ions in the composite coating and its lethal effect on marine organisms (especially N. closterium) to verify its antifouling performance.

3. **Analyzing the Microstructure and Composition of the Coating**: Using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and X-ray diffraction (XRD), the microstructure and compositional changes of the composite coating are characterized to explore its corrosion resistance and antifouling mechanisms.

4. **Electrochemical Performance Testing**: Through potentiodynamic polarization curves (PDP) and electrochemical impedance spectroscopy (EIS), the electrochemical performance of the composite coating is evaluated to further verify its corrosion resistance effect.

Through these studies, the paper aims to develop a composite coating that possesses both excellent corrosion resistance and good antifouling effects, thereby extending the service life of Q235 steel in marine environments.