Abstract:Carbon fiber reinforced polymer (CFRP) composites are popular materials in the aerospace and automotive industries because of their low weight, high strength, and corrosion resistance. However, wrinkles or geometric distortions in the composite layers significantly reduce their mechanical performance and structural integrity. This paper presents a method for non-destructively extracting the three-dimensional geometry, lamina by lamina, of a laminated composite. A method is introduced for fabricating consistent out-of-plane wrinkled CFRP laminate panels, simulating the in-service wrinkle observed in industries that utilize thick structure composites such as the vertical lift or wind power industries. The individual lamina geometries are extracted from the fabricated coupon with an embedded wrinkle from captured ultrasonic waveforms generated from single-element conventional ultrasonic (UT) scan data. From the extracted waveforms, a method is presented to characterize the wrinkle features within each individual lamina, specifically the spatially varying wrinkle height and intensity for the wrinkle. Parts were fabricated with visibly undetectable wrinkles using a wet layup process and a hot press for curing. Scans were performed in a conventional immersion tank scanning system, and the scan data were analyzed for wrinkle detection and characterization. Extraction of the layers was performed based on tracking the voltage peaks from A-scans in the time domain. Spatial Gaussian averaging was performed to smooth the A-scans, from which the surfaces were extracted for each individual lamina. The extracted winkle surface aligned with the anticipated wrinkle geometry, and a single parameter for quantification of the wrinkle intensity for each lamina is presented.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is how to non - destructively quantify the wrinkle characteristics inside laminates in carbon - fiber - reinforced polymer (CFRP) composites. Specifically, the paper proposes a method to extract and analyze the three - dimensional geometric structure in CFRP laminates, especially the wrinkle height and intensity between layers, through high - resolution ultrasonic technology. This method can be used to detect and evaluate wrinkles that are difficult to perceive with the naked eye and are generated during the manufacturing process. These wrinkles can significantly reduce the mechanical properties and structural integrity of the composites. Through this method, researchers hope to provide an effective tool to ensure the quality and performance of CFRP composites, especially for applications in the aerospace and automotive industries.

High-Resolution Ultrasound to Quantify Sub-Surface Wrinkles in a Woven CFRP Laminate

Understanding the Impact of Fibre Wrinkle Architectures on Composite Laminates Through Tailored Gaps and Overlaps

Nondestructive Detection of In-Plane Wrinkles in Carbon Fiber Laminates Using Eddy Current and Ultrasonic Testing

A Multivariate Statistical Approach to Wrinkling Detection in Composites

Investigation on the Compressive Mechanical Properties of Ultra-Thick CFRP Laminates

Advances in Automated Eddy-Current Characterisation of Carbon Fibre Composites

Influences of Wrinkles Induced by Tows’ Offset in Automated Fiber Placement on the Bending Properties of Composites

Wrinkle Detection in Carbon Fiber-Reinforced Polymers Using Linear Phase FIR-Filtered Ultrasonic Array Data

Damage and Failure Mechanisms of CFRP Due to Manufacturing Induced Wrinkling Defects

Assessment of the 3D Ply-by-ply Fiber Structure in Impacted CFRP by Means of Planar Ultrasound Computed Tomography (Pu-Ct)

Quantitative Evaluation of the Severity of Wrinkles in Carbon Fiber Composites

A robust and automated method for geometric modelling of thick laminates with multiple and asymmetric ply wrinkles

Point-cloud acquisition in CFRP composites using ultrasonic location estimation with the phase-shift reference pulse

Experimental investigation of trans-scale displacement responses of wrinkle defects in fiber-reinforced composite laminates

Automated image-based geometric modelling of thick laminates with three-dimensional ply wrinkles

Non-Destructive Evaluation of In-Plane Waviness in Carbon Fiber Laminates Using Eddy Current Testing

Characterization of wrinkle morphologies by surface waviness evaluation method during deep forming of multilayer composite preforms

3D photothermal reconstruction of subsurface defects in notched multidirectional CFRP laminates due to tensile fatigue loading

Comparative Study of Ultrasonic Techniques for Reconstructing the Multilayer Structure of Composites

Phased array ultrasonic inspection and automated identification of wrinkles in laminated composites

Experimental Method to Determine the Draping Behavior of Auxiliary Materials for the Vacuum Bagging of CFRP Parts on Doubled-Curved Surfaces