Abstract:In this study, a method for detecting defects in carbon fiber‐reinforced polymers (CFRPs) using a new probe to measure eddy current loss is proposed. The comparison of eddy current loss among different types of CFRPs is presented, scanning imaging results of orthogonally woven CFRP sample further demonstrate the detection performance, and the fiber orientation of CFRPs is characterized. Eddy current testing (ECT) is a widely used technique for detecting defects in carbon fiber‐reinforced polymers (CFRPs) at high frequencies. However, designing high‐frequency systems can be challenging, and high noise levels can be problematic. To address these issues, non‐destructive testing (NDT) methods that can detect CFRP defects at lower frequencies must be explored. In this study, a novel NDT method for detecting defects in CFRP at low frequencies was proposed. This method is an alternative to pulsed eddy current thermography and can achieve similar detection and imaging results at low frequencies. Furthermore, the developed method has a simpler structure and is easier to implement. This method uses the eddy current loss to characterize the thermal power of the eddy current in CFRP. A new probe was used to detect the eddy current loss to inspect the CFRP. The effectiveness of the proposed method was experimentally verified using different types of CFRP samples based on the C‐scan technology. The scanned images demonstrate that the developed method can provide appropriate detection results up to a frequency of 750 kHz. Furthermore, rotation experiments were performed to detect the fiber direction; the proposed method successfully detected the fiber direction up to 750 kHz. Thus, the proposed method can improve the detection of defects and enhance the longevity of CFRP components. Future work will focus on enhancing the sensitivity of this method at even lower frequencies.

Nondestructive Detection of In-Plane Wrinkles in Carbon Fiber Laminates Using Eddy Current and Ultrasonic Testing

Non-Destructive Evaluation of In-Plane Waviness in Carbon Fiber Laminates Using Eddy Current Testing

Advances in Automated Eddy-Current Characterisation of Carbon Fibre Composites

Understanding the Impact of Fibre Wrinkle Architectures on Composite Laminates Through Tailored Gaps and Overlaps

High-Resolution Ultrasound to Quantify Sub-Surface Wrinkles in a Woven CFRP Laminate

A Multivariate Statistical Approach to Wrinkling Detection in Composites

Thickness Measurement of Composite Material Using Eddy Current Testing

Eddy current non-destructive evaluation of manufacturing flaws and operational damage in CFRP composites

Influences of Wrinkles Induced by Tows’ Offset in Automated Fiber Placement on the Bending Properties of Composites

Directional eddy current probe configuration for in-line detection of out-of-plane wrinkles

Detectability Evaluation of Eddy Current Testing Probes for Inspection of Defects in Carbon Fiber Reinforced Polymer Laminates

Wrinkles in Fiber-Reinforced Resin Composites: Micro-stress Non-Destructive Testing

Damage and Failure Mechanisms of CFRP Due to Manufacturing Induced Wrinkling Defects

Assessment of the 3D Ply-by-ply Fiber Structure in Impacted CFRP by Means of Planar Ultrasound Computed Tomography (Pu-Ct)

Reconstruction of Cracks in a Carbon Fiber-Reinforced Polymer Laminate Plate from Signals of Eddy Current Testing

Experimental investigation of trans-scale displacement responses of wrinkle defects in fiber-reinforced composite laminates

Ultrasonic Testing of Carbon Fiber-Reinforced Polymer Composites

Wrinkle defects investigation on displacement response in fiber-reinforced composites using grating projection measurement

A novel assessment method for wrinkle defects in composites

A new probe‐based electromagnetic non‐destructive testing method for carbon fiber‐reinforced polymers utilizing eddy current loss measurements

Automated Quantification of Interlaminar Delaminations in Carbon-Fiber-Reinforced Polymers via High-Resolution Ultrasonic Testing