Abstract:Wrinkle defects were found widely exist in the field of industrial products, i.e. wind turbine blades and filament-wound composite pressure vessels. The magnitude of wrinkle wavelength varies from several millimeters to over one hundred millimeters. Locating the wrinkle defects and measuring their responses are very important to the assessment of the structures that containing wrinkle defects. A meso-mechanical modeling is presented based on the homogenization method to obtain the effective stiffness of a graded wrinkle. The finite element simulation predicts the trans-scale response of out-of-plane displacement of wrinkled laminates, where the maximum displacement ranges from nanoscale to millimeter scale. Such trans-scale effect requires different measurement approaches to observe the displacement responses. Here we employed Shearography (Speckle Pattern Shearing Interferometry) and fringe projection profilometry (FPP) method respectively according to the different magnitude of displacement. In FPP method, a displacement extraction algorithm was presented to obtain the out-of-plane displacement. The measurement sensitivity and accuracy of Shearography and FPP are compared, which provides a quantitative reference for industrial non-destructive test.

What problem does this paper attempt to address?

This paper attempts to solve the problem of cross - scale displacement response of wrinkle defects in fiber - reinforced composite laminates. Specifically, the research focuses on the following aspects: 1. **Widespread Existence and Influence of Wrinkle Defects**: Wrinkle defects are common in industrial products, especially in wind turbine blades and filament - wound composite pressure vessels. These defects will affect the strength, stiffness and fatigue life of the structure. Therefore, accurately locating and measuring the response of these defects is crucial for evaluating the structure containing wrinkle defects. 2. **Cross - scale Displacement Response**: The wavelength of wrinkles ranges from a few millimeters to more than 100 millimeters, and its displacement response also spans different scales from the nanometer level to the millimeter level. This cross - scale effect requires the use of different measurement methods to observe the displacement response. 3. **Selection and Comparison of Measurement Methods**: The paper adopts two main measurement methods - shearography and fringe projection profilometry (FPP). Shearography is suitable for high - sensitivity measurement of nanometer - level displacements, while the FPP method is suitable for displacement measurement at the millimeter level and above. By experimentally comparing the sensitivity and accuracy of these two methods, a quantitative reference is provided for industrial non - destructive testing. 4. **Finite Element Analysis**: Based on the micromechanical model, the out - of - plane displacement response of wrinkled laminates is predicted by finite - element simulation. The simulation results show that the out - of - plane displacement in the wrinkled area is very sensitive to tensile loads, and the maximum displacement ranges from 102 nanometers to 106 nanometers. 5. **Experimental Verification**: The results of finite - element analysis are verified by experiments, and the performance of different measurement methods is compared. The experimental results show that the sensitivity of shearography on low - thickness specimens is much higher than that of the FPP method, but in the case of large deformations, the FPP method has an advantage. In summary, this paper aims to comprehensively study the cross - scale displacement response of wrinkle defects in fiber - reinforced composites by establishing a micromechanical model of wrinkle defects, combining finite - element analysis and experimental verification, and providing a reliable basis for the selection of measurement methods in industrial applications.

Experimental investigation of trans-scale displacement responses of wrinkle defects in fiber reinforced composite laminates

Experimental investigation of trans-scale displacement responses of wrinkle defects in fiber-reinforced composite laminates

Understanding the Impact of Fibre Wrinkle Architectures on Composite Laminates Through Tailored Gaps and Overlaps

Progressive failure analysis of 2D woven composites at the meso-micro scale

Influences of Wrinkles Induced by Tows’ Offset in Automated Fiber Placement on the Bending Properties of Composites

Wrinkle defects investigation on displacement response in fiber-reinforced composites using grating projection measurement

Wrinkles in Fiber-Reinforced Resin Composites: Micro-stress Non-Destructive Testing

A novel assessment method for wrinkle defects in composites

Effect of Eccentric Tension on the Response of Wrinkle Defects in Carbon Fiber-Reinforced Composite Laminates

Damage and Failure Mechanisms of CFRP Due to Manufacturing Induced Wrinkling Defects

An experimental and computational investigation of embedded wrinkle's impacts on the compressive responses of thick unidirectional glass fiber-reinforced composites

Deformation and Fracture Mechanisms of Automated Fiber Placement Pre-Preg Laminates under Out-of-plane Tensile Loading

Quantitative Evaluation of the Severity of Wrinkles in Carbon Fiber Composites

Wrinkles in Fiber-Reinforced Resin Composites: Heterogeneity and Virtual Test

The effects of wrinkle distributions on the mechanical characteristics of unidirectional glass fiber-reinforced composites

Virtual Testing of Mechanical Response of Composite Plates with Normally Distributed Wrinkles

Modeling on the Effect of Automated Fiber Placement Induced Gaps in Curved Composite Laminates

Characterization of wrinkle morphologies by surface waviness evaluation method during deep forming of multilayer composite preforms

Dynamic Deformation Measurement of Woven Composite with Edge Cracks

A robust and automated method for geometric modelling of thick laminates with multiple and asymmetric ply wrinkles

Numerical and Experimental Investigation on Mechanical Responses of Plain Woven CFRP Composite under Various Loading Cases