Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Study on mechanism of differential concentration corrosion

The Impact of Oxygen Availability on Steel Corrosion Considering the Self-Balance Between Anodic and Cathodic Corrosion Cells

A Mechanistic Model for Pipeline Steel Corrosion in Supercritical CO2–SO2–O2–H2O Environments

Mechanism analysis, anti-corrosion techniques and numerical modeling of corrosion in energy industry

Localized corrosion behavior on a heterogeneous surface involving multicomponent reactive transport and morphology evolution

Study on the Time-Dependent Evolution of Pitting Corrosion in Flowing Environment

Assessment by finite element modelling of the mechano-electrochemical interaction at double-ellipsoidal corrosion defect with varied inclinations on pipelines

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Development of a finite element model for simulation and prediction of mechanoelectrochemical effect of pipeline corrosion

Study on corrosion simulation and anti-corrosion of marine B10 seawater pipe system

Electrochemical and Stress Corrosion Mechanism of Submarine Pipeline in Simulated Seawater in Presence of Different Alternating Current Densities

Numerical Simulation of Stray Current Corrosion of Buried Steel Pipeline under Cathodic Protection

A fully coupled model of hydrodynamic-chemical-electrochemical processes for CO2 uniform corrosion in multi-physics environment

Numerical modeling of stray current corrosion of ductile iron pipe induced by foreign cathodic protection system

Study on Mechanism of Bio-Antifouling by Impressed Cathode Current in Seawater Pipe

Multi-Physics Coupling Analysis on the Time-Dependent Localized Corrosion Behavior of Carbon Steel in CO2-H2O Environment

Corrosion Behavior of X80 Steel in a Simulated Soil Solution Under Square-Wave Current Interference

Investigation by numerical modeling of the mechano-electrochemical interaction of circumferentially aligned corrosion defects on pipelines

Understanding and Probing Progression of Localized Corrosion on Inner Walls of Steel Pipelines: an Overview

Multiscale characterization of seawater pipe erosion of B10 copper-nickel alloy welded joints

Influence of the Dissolved Oxygen Concentration in Artificial Seawater on the Corrosion Behavior of Q235 Mild Steel