Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

A Mechanistic Model for Pipeline Steel Corrosion in Supercritical CO2–SO2–O2–H2O Environments

Main control factors and prediction model of flow-accelerated CO2/H2S synergistic corrosion for X65 steel

The Impact of Oxygen Availability on Steel Corrosion Considering the Self-Balance Between Anodic and Cathodic Corrosion Cells

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

A fully coupled model of hydrodynamic-chemical-electrochemical processes for CO2 uniform corrosion in multi-physics environment

Mechanical model and probability analysis of buried pipelines failure under uniform corrosion

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Study on corrosion properties of pipelines in simulated produced water saturated with supercritical CO2

Modelling and Analysis of the Corrosion Characteristics of Ferritic-Martensitic Steels in Supercritical Water

Mechanism analysis, anti-corrosion techniques and numerical modeling of corrosion in energy industry

Study on mechanism of differential concentration corrosion

The Upper Limit of Moisture Content for Supercritical CO2 Pipeline Transport

Regression Model of Factors Influencing the Corrosion Rate of X80 Steel in Silt Based on an Orthogonal Test

Corrosion Behavior of X80 Steel in a Simulated Soil Solution Under Square-Wave Current Interference

Impact of Surface Roughness and Humidity on X70 Steel Corrosion in Supercritical CO2 Mixture with SO2, H2O, and O2

Effect of H2O Content on the Corrosion Behavior of X52 Steel in Supercritical CO2 Streams Containing O2, H2S, SO2 and NO2 Impurities

CFD-Based Erosion and Corrosion Modeling of a Pipeline with CO2-Containing Gas–Water Two-Phase Flow

Microbial corrosion behavior of pipeline steels in simulation environment of natural gas transportation pipeline

Effect of High-Concentration O2on Corrosion Behavior of X70 Steel in Water-Containing Supercritical CO2with SO2

A comprehensive review of metal corrosion in a supercritical CO2 environment

Corrosion behaviour of X80 pipeline steel welded joint in H2O- saturated supercritical-CO2 environment