Abstract:Purpose The majority of machine component failures are caused by load conditions that change with time. Under those circumstances, the component can function effectively for a long time but then breaks down unexpectedly and without warning. Therefore, the study of fatigue considerations in design becomes important. Also, to determine the component's long-term tenability, fatigue behavior must be investigated. This paper aims to investigate the fatigue life of aluminum 6061-T6 alloy under uniaxial loading using experiments and finite element simulation. Design/methodology/approach Both base metal (BM) and friction stir welding (FSW) configurations have been used to analyze fatigue behavior. The experimental tests were carried out using Instron-8801 hydraulic fatigue testing machine at frequency of 20 Hz and load ratio of 0.1. The yield strength, ultimate tensile strength, amplitude stress and fatigue life were used as input in simulation analysis software. Based on the findings of the tensile test, the maximum stress applied during the fatigue testing was estimated. Simulated and experimental results were also used to plot and validate the S-N curves. The fracture behavior of specimens was also examined using fractographic analysis. Findings The fractured surfaces indicate both brittle and ductile failure in the specimens. However, dimples dominated during the final fracture. The comparison between experimental and simulation results illustrates that the difference in fatigue cycles increases with an increase in the yield strength of both BM and FSWed specimens. This disparity is attributed to many factors such as scratches, rough surfaces and microstructural behavior. Aluminum 6061-T6 alloy is considered a noteworthy material where high strength with reduced weight contributes to the crash-worthy design of automobile structures. Originality/value The current study is significant in the prediction of the fatigue life of aluminum 6061-T6 alloy using experiments and simulation analysis. A good correlation was found when the experimental and simulation analysis were compared. The proposed simulation analysis approach can be used to anticipate a component's fatigue life.

Characterization of High-Cycle Bending Fatigue Behaviors for Piston Aluminum Matrix SiO2 Nano-composites in Comparison with Aluminum–Silicon Alloys

Microstructural and thermal properties of piston aluminum alloy reinforced by nano-particles

Effect of nano-clay addition and heat-treatment on tensile and stress-controlled low-cycle fatigue behaviors of aluminum-silicon alloy: Effect of nano-clay addition and heat-treatment

Impacts of nano-clay particles and heat-treating on out-of-phase thermo-mechanical fatigue characteristics in piston aluminum-silicon alloys

High-cycle fatigue of a metal matrix composite based on an aluminum alloy 7075-T1 reinforced with silicon carbide particles

Significantly enhanced fatigue resistance and mechanisms of hypoeutectic Al-Si composite calibrated using trace in-situ nanocrystals

High-cycle fatigue failure analysis of cast Al-Si alloy engine cylinder head

Sensitivity analysis of mechanical properties and ductile/brittle behaviors in aluminum‐silicon alloy to loading rate and nano‐particles, considering interaction effects

Plain and fretting fatigue characteristics of 16MnCr5 steel under cyclic bending loading with the application of the engine piston pin

Achieving ultrahigh fatigue resistance in AlSi10Mg alloy by additive manufacturing

Fatigue behavior and damage analysis of PIP C/SiC composite

Experiment and numerical simulation study of thermal fatigue of an aluminum alloy piston

Experimental and simulation analysis of fatigue life of aluminum 6061-T6 alloy

Estimation of Low-Cycle Fatigue Lifetime in Aluminum-Silicon-Magnesium Alloy of Cylinder Heads based on Striation Marks as Failure Features of Fracture Surfaces and Paris Crack Growth Law

Mechanical Test on Aluminum Alloy with Maximal Soluble SiC Reinforcement

The Effect of Micro-SiCp Content on the Tensile and Fatigue Behavior of AZ61 Magnesium Alloy Matrix Composites

The influence of GNP and nano-silica additives on fatigue life and crack initiation phase of Al-GFRP bonded lap joints subjected to four-point bending

Effect of machined surface integrity on fatigue resistance of aluminum-silicon alloy ZL109

Microstructure related analysis of tensile and fatigue properties for sand casting aluminum alloy cylinder head

Mechanical Properties as a Function of Casting Process of Aluminum–Silicon Alloy Matrix Composites

Mechanical Properties of Aluminum-4043/Nickel-coated Silicon Carbide Composites Produced via Stir Casting