Abstract:Sticking of alumina as well as spinel inclusions inside the sub-entry nozzles as well as tundish nozzle is a perennial problem during continuous casting of aluminum-killed steel through billet casters. This results in restriction or complete blockage of flow of liquid steel through the nozzles eventually leading to abortion of sequence in billet casters and stopping of continuous casting machine. Nozzle clogging not only restricts the productivity by restraining the casting sequence, intermittent extrication of clogged alumina particles or dislodged refractory materials which are a significant source of non-metallic macro-inclusions in the cast sections of billet casters. If these inclusions are not removed completely during secondary refining of steel, they cause excessive clogging mainly in low-carbon Al-killed steels. In other grades of Al-killed steel, clogging is also very prominent if the deoxidation and secondary refining is not carried out properly. IISCO Steel Plant (ISP), Burnpur, a new, modernized unit of Steel Authority of India Limited, was facing problems of nozzle clogging in low-carbon, low-Si, Al-killed grade (EWNR—electrode quality grade) resulting in premature abortion of casting sequence leading to huge productivity loss. To solve the problem of nozzle clogging in low-carbon Al-killed grades and other grades at ISP, optimization of various steelmaking parameters, viz., amount of Al addition and its sequence, purging regime in ladle furnace, optimization of Ca treatment process, etc. has been carried out which has resulted in improvement in castability of Al-killed steel in billet caster of ISP.

Insights into Non-free Opening of Ladles: Filler Sand Chemistry Modifications for High Mn Steel Billet Casting

Free Opening Performance of Steel Ladle as a Function of Filler Sand Properties

Effect of Chromite-Silica Sands Characteristics on Performance of Ladle Filler Sands for Continuous Casting

Improvement of free-opening rate of ladle tapping at the same side

Sintering Behavior of New Chromite-Alumina Mixed Ladle Filler Sands for High Mn-High Al Steel Grades

Laboratory investigation on quantitative effect of ladle filler sands on the cleanliness of a bearing steel

Computational study of non-isothermal slag eye formation and its effects on ladle refining

Effect of Carbon on Sintering Behavior of Chromite‐Based Ladle Filler Sands

Mechanism Study of the Blocking of Ladle Well Due to Sintering of Filler Sand

Effect of silica concentration on degree of sintering of chromite-silica ladle well filler sand based on South African raw materials

Impact of slag–refractory lining reactions on the formation of inclusions in steel

Improvement in Castability of Al-Killed Steel in Billet Casters by Process Optimization

Effects of gating design on structural and mechanical properties of high manganese steel by optimizing casting process parameters

Improvement in Castability of Al Killed Steel in Billet Casters by Process Optimisation

Laboratory Study on the Sintering Behavior of Zircon‐Based Ladle Filler Sands

Unveiling the effect of MnO/SiO2 ratios on the viscosity and structure of mold fluxes for high-Mn cryogenic steels

Deep Insight into Mold Level Fluctuation During Casting Different Steel Grades

Elimination of Fluorspar Use and Reduction in Lime Consumption at Ladle Furnace by Reutilizing Alumina-Rich Ladle Furnace Slag