Abstract:Ladle furnace slag (LFS), a by-product of steel refining, shows a promising reuse pathway as an alternative additive or substitute for Portland cement due to its high alkalinity and similar chemical composition to clinkers. However, LFS is often stored in large, open surface areas, leading to many environmental issues. To tackle waste management challenges, LFS can be recycled as supplementary cementitious material (SCM) in many cementitious composites. However, LFS contains some mineral phases that hinder its reactivity (dicalcium silicate (γ-C2S)) and pose long-term durability issues in the cured cemented final product (free lime (f-CaO) and free magnesia (f-MgO)). Therefore, LFS needs to be adequately treated to enhance its reactivity and ensure long-term durability in the structures of the cementitious materials. This literature review assesses possible LFS treatments to enhance its suitability for valorization. Traditional reviews are often multidisciplinary and explore all types of iron and steel slags, sometimes including the recycling of LFS in the steel industry. As the reuse of industrial by-products requires a knowledge of their characteristics, this paper focuses first on LFS characterization, then on the obstacles to its use, and finally compiles an exhaustive inventory of previously investigated treatments. The main parameters for treatment evaluation are the mineralogical composition of treated LFS and the unconfined compressive strength (UCS) of the final geo-composite in the short and long term. This review indicates that the treatment of LFS using rapid air/water quenching at the end-of-refining process is most appropriate, allowing a nearly amorphous slag to be obtained, which is therefore suitable for use as a SCM. Moreover, the open-air watering treatment leads to an optimal content of treated LFS. Recycling LFS in this manner can reduce OPC consumption, solve the problem of limited availability of blast furnace slag (GGBFS) by partially replacing this material, conserve natural resources, and reduce the carbon footprint of cementitious material operations.

Elimination of Fluorspar Use and Reduction in Lime Consumption at Ladle Furnace by Reutilizing Alumina-Rich Ladle Furnace Slag

Recycling Ladle Furnace Slag as Flux in Steelmaking: A Review

Desulphurization of Hot Metal and Ferronickel with Calcium Aluminate Fluxes

Characterization of Ladle Furnace Slag from Carbon Steel Production as a Potential Adsorbent

Evaluating the Effect of MgO/Al2O3 Ratio on Thermal Behaviors and Structures of Blast Furnace Slag with Low Carbon Consumption

Effect of CaO/Al2O3 Ratio in Fluorine‐Free Refining Slag with Low Basicity on the Cleanliness of SWRS82B Steel

A Clean Disposal Method of Carbide Slag with Carbon Emission Reduction: Used As a Flux for Iron Ore Sintering

Selective extraction of lithium and solidified fluoride from overhaul slag by the calcium sulfate roasting and water leaching

Influence of Slag and Refractory Materials on Inclusions during the Ladle Refining of Low Carbon Aluminum Killed Steel

A Strategy for Partial Replacement of Lime by Limestone and Its Impact on Basic Oxygen Furnace Steelmaking

Generation, utilization, and environmental impact of ladle furnace slag: A minor review

Processes of salt slag recycling in aluminum production to obtain powder material with a high content of aluminum oxide phases

Fluorine Fixation During the Co-treatment of Spent Cathode Carbon and Copper Slag

Manganese and Aluminium Recovery from Ferromanganese Slag and Al White Dross by a High Temperature Smelting-Reduction Process

A novel approach to accelerate carbon dioxide sequestration of ladle furnace slag using sodium bicarbonate solution

Properties of Fluorine-Free Steelmaking Flux Prepared Using Red Mud

Advances in chemical and physical properties of electric arc furnace carbon steel slag by hot stage processing and mineral mixing

Potential Reuse of Ladle Furnace Slag as Cementitious Material: A Literature Review of Generation, Characterization, and Processing Methods

Directional sulfur removal from ladle furnace slag by electric field strengthening treatment

Fluoride vaporization and crystallization of CaF2–CaO–Al2O3–(La2O3) slag for vacuum electroslag remelting

Iron and copper recovery from copper slags through smelting with waste cathode carbon from aluminium electrolysis