Synthesis and Magnetic Properties of Amorphous Fe–Y–B Thin Films
S. Y. Liu,Q. P. Cao,S. Mori,K. Ishigami,K. Igarashi,C. Wang,X. Qian,X. D. Wang,D. X. Zhang,B. Riedmueller,U. Herr,H. -J. Fecht,X. L. Li,Y. W. Du,J. Zhao,Y. Z. Fang,Q. Tao,J. Z. Jiang
DOI: https://doi.org/10.1016/j.jallcom.2014.04.018
IF: 6.2
2014-01-01
Journal of Alloys and Compounds
Abstract:Amorphous Fe-Y-B thin films have been successfully fabricated by direct-current magnetron sputtering, and the effects of annealing treatment on the microstructure and magnetic properties, especially coercivity and magneto-impedance ratio, were investigated systematically. After low-temperature heat treatments (below 673 K), films still remain amorphous structure and their magnetic properties were largely enhanced due to stress release, e. g., the maximum magneto-impedance ratio increases from about 5.6-46.6% and the coercivity decreases from about 7.7-2.2 Oe for as-deposited film and the film annealed at 573 K for 1 h, respectively. After high-temperature heat treatment at 673 K, crystallization occurs, deteriorating magnetic properties (magnetic softness and magneto-impedance features) of the film. The Fe-Y-B thin film annealed at 573 K for 1 h, possessing good magneto-impedance effect and soft magnetic properties, might have potential application in micro-sized magnetic actuators. (C) 2014 Elsevier B.V. All rights reserved.