Abstract:Melt-spun amorphous Fe73.5Cu1Nb3Si13.5B9 (FINEMET, at%) ribbons were ball-milled to obtain powder. The powder was sieved and then passivated in 0.2 similar to 1.0% phosphoric acid solution to form a well-coated passivator layer, followed by cold compaction under the pressure of 1.64 similar to 1.96 GPa to prepare toroidal magnetic cores. The powder cores were annealed at 400 similar to 600 degrees C to relieve the internal stress and to optimize the crystalline grain size. After annealed at 500 degrees C for 1 h, alpha-Fe(Si) crystallites with an average grain size of 14.3 nm were embedded in the amorphous matrix. Combined with the insulation of each powder and the two-phase structure, the powder core exhibits excellent magnetic properties.

Fabrication and Magnetic Properties of FINEMET Alloy Powder Cores