Abstract:In this paper, an alumina ink with good rheological properties was successfully prepared using pseudoboehmite as the main component, nitric acid as the colloidal solvent, and sesbania powder as the lubricant. The impact of nine different ink formulations, namely, Ink1 to Ink9, on the printability and rheological features of the ink was investigated. Consequently, it was found that Ink3 with 5 wt % nitric acid and 5 wt % sesbania powder exhibited the most favorable formability. This ink was utilized to fabricate alumina samples with direct ink writing (DIW) three-dimensional (3D) printing technology. The printed alumina samples were characterized using an automatic Brunauer-Emmett-Teller, X-ray diffractometer, Fourier transform infrared spectroscopy, and scanning electron microscope. To obtain the optimal printing parameters, a three-factor and three-level orthogonal test was designed to research the influences of different 3D printing parameters (filling ratio, nozzle diameter, and layer thickness) on the specific surface area, pore characteristics (size and volume), and radial crushing strength of the alumina specimens. The primary and secondary orders of the effects on the radial crushing strength and pore structure were determined through analysis of the experimental data. The experimental results showed that the alumina sample with a filling ratio of 80%, nozzle diameter of 0.6 mm, and layer thickness of 0.3 mm was found to have better strength of 48.07 ± 9.53 N/mm and specific surface area of 185.7315 m<sup>2</sup>/g. This study provides a theoretical base for the preparation of alumina carriers by DIW 3D printing.

Chemical etching optimization of 3D printed α-Al 2 O 3 monoliths to enhance the catalytic applications

Overcoming the limitations of anthracene alkylation using SZ-DeAl-DFNS acid catalyst

Direct ink writing of Pd-Decorated Al<sub>2</sub>O<sub>3</sub> ceramic based catalytic reduction continuous flow reactor

Optimization of the sintering thermal treatment and the ceramic ink used in direct ink writing of α-Al2O3: Characterization and catalytic application

Towards unconstrained catalyst shaping: high accuracy DLP printing of porous γ-Al2O3-based catalysts

Direct Ink Writing of Hierarchical Porous SiC Ceramics As Catalyst Support for Hydrogen Production

Novel ceramic supports for catalyst with hierarchical pore structures fabricated via additive manufacturing-direct ink writing

3D Printing and Chemical Dealloying of a Hierarchically Micro- and Nanoporous Catalyst for Wastewater Purification

Impact of Co impregnation on 3D printed alumina supports and effects on Fischer-Tropsch reaction

Fabrication of γ-Al2O3 Nanoarrays on Aluminum Foam Assisted by Hydroxide for Monolith Catalysts

3D printed hierarchical spinel monolithic catalysts for highly efficient semi-hydrogenation of acetylene

Direct ink writing of Pd-Decorated Al2O3 ceramic based catalytic reduction continuous flow reactor

Optimization of 3D Printing Parameters for Alumina Ceramic Based on the Orthogonal Test

Exploring the 3D printing of molybdenum carbide-based catalysts for the reverse water gas shift reaction: A multi scale study

3D printed Ni/Al2O3 based catalysts for CO2 methanation - a comparative and operando XRD-CT study

Tailored monolithic catalyst and reactor by direct photo-curing 3D printing for oxidative desulfurization of fuels

First Insight into the Catalytic Activity of Stereolithographically 3D‐printed Tannin‐based Carbon Architectures

Optimization of Metal-Assisted Etchant Components for Fabrication of Porous Silicon

Stereolithography 3D printed monolithic catalyst for highly efficient oxidative desulfurization of fuels

The Effects of Acid Etching on the Morphology and Properties of Medical Grade Alumina and Zirconia Surfaces for Prosthetics

Sponge-like carbon monoliths: Porosity control of 3D-printed carbon supports and its influence on the catalytic performance