Abstract:In this study, amorphous + nanocrystalline Ti-BN mixed powders were obtained through first-step mechanical alloying; subsequently, almost completely amorphous SiBCN-Ti mixed powders were achieved in the second-step milling. The SiBCN-Ti bulk ceramics were consolidated through hot pressing sintering at 1900 °C/60 MPa/30 min, and the microstructural evolution and mechanical properties of the as-sintered composite ceramics were investigated using SEM, XRD, and TEM techniques. The as-sintered SiBCN-Ti bulk ceramics consisted of substantial nanosized BN(C), SiC, and Ti(C, N) with a small amount of Si2N2O and TiB2. The crystallized BN(C) enwrapped both SiC and Ti(C, N), thus effectively inhibiting the rapid growth of SiC and Ti(C, N). The sizes of SiC were ~70 nm, while the sizes of Ti(C, N) were below 30 nm, and the sizes of Si2N2O were over 100 nm. The SiBCN-20 wt.% Ti bulk ceramics obtained the highest flexural strength of 394.0 ± 19.0 MPa; however, the SiBCN-30 wt.% Ti bulk ceramics exhibited the optimized fracture toughness of 3.95 ± 0.21 GPa·cm1/2, Vickers hardness of 4.7 ± 0.27 GPa, Young's modulus of 184.2 ± 8.2 GPa, and a bulk density of 2.85 g/cm3. The addition of metal Ti into a SiBCN ceramic matrix seems to be an effective strategy for microstructure optimization and the tuning of mechanical properties, thus providing design ideas for further research regarding this family of ceramic materials.

Densification behavior and microstructure development in TiB2 ceramics doped with h-BN

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

Role of co-addition of BN and SiC on microstructure of TiB2-based composites densified by SPS method

A microstructural approach to the chemical reactions during the spark plasma sintering of novel TiC–BN ceramics

High pressure sintering behavior and mechanical properties of cBN-Ti 3Al and cBN-Ti 3Al-Al composite materials

Microstructural characterization of TiB2–SiC–BN ceramics prepared by hot pressing

Influence of TiB2 and CrB2 on densification, microstructure, and mechanical properties of ZrB2 ceramics

Microstructure and Mechanical Properties of TiN–TiB2–hBN Composites Fabricated by Reactive Hot Pressing Using TiN–B Mixture

Fabrication of (Zr,Ti)B2-ZrN-BN composites through reactive spark plasma sintering of ZrB2 and TiN

Synthesis of TiN–TiB2–hBN composite powders with a core-shell structure and preparation of bulk samples

Densification, Microstructure, and Wear Properties of TiB2-TiC-GNP and TiB2-TiC-BN Composites

Effects of TiB2 Particles on the Microstructure Evolution and Mechanical Properties of B4C/TiB2 Ceramic Composite

A Novel TiB2–SiC Composite Doped with Diamond Nanoparticles: Densification, Microstructure, and Thermal Properties

Quantitative analysis and comparison on densification kinetics and grain growth mechanisms using reactively and directly densified TiB 2 -SiC- h BN ceramics

Pulsed electric current sintering of TiB2-based ceramics using nitride additives

Effects of Ti on the Microstructural Evolution and Mechanical Property of the SiBCN-Ti Composite Ceramics

Reaction Sintering of Machinable TiB2-BN-C Ceramics with In-Situ Formed h-BN Nanostructure

TiB2 effects on the AlMgB14–TiB2 ceramics structure and properties

Densification and mechanical properties of boron carbide prepared via spark plasma sintering with cubic boron nitride as an additive

Influence of TiN addition on densification behavior and mechanical properties of ZrB2 ceramics

Spark plasma sintering of TiN–TiB2–hBN composites and their properties