Effects of Curing Temperature on Expansion of Concrete Due to ASR

Yongfu Yang,Min Deng,Liwu Mo,Wei Li

DOI: https://doi.org/10.3390/ma17133140

IF: 3.4

2024-06-28

Materials

Abstract:In the laboratory study of alkali–silica reaction (ASR), models attempt to predict the service life of concrete due to ASR by correlating the performance of concrete at high and low temperatures. However, the consequences of elevating temperature are not so encouraging. In this paper, the influence of temperature on the expansion of 2-graded concrete and 3-graded concrete caused by ASR was investigated by curing the concrete under different temperatures ranging from 40 °C to 80 °C. Increased temperature resulted in rapid expansion at the early stages, but the expansion rate of concrete prisms cured at the higher temperatures (70 °C and 80 °C) was slowed down at the later stages, and concrete prisms cured at 50 °C or 60 °C showed the highest expansions during the experimental period. The chemical analysis results of the pore solution expressed from the concrete show that the ASR expansion is significantly influenced by the [OH−]: the decrease in [OH−] leads to the retardation of the ASR expansion. The decrease in [OH−] is attributed to the consumption of OH− ions for the alkali–silica reaction and the decrease in activity of NaOH(aq) influenced by the temperature. For large cross-section specimens, the OH− within the concrete for alkali–silica reactions cannot be effectively compensated by the external alkali solution. In the accelerated test to evaluate ASR for large cross-section specimens, a curing temperature of less than 60 °C is suggested. This study provides critical insights into the temperature dependency of ASR expansion of concrete, offering a curing temperature range for developing predictive models of ASR expansion under varied environmental conditions.

materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to explore the influence of different curing temperatures on the expansion of concrete caused by alkali - silica reaction (ASR). Specifically, the researchers evaluated the influence of temperature on the ASR expansion rate and the final expansion amount by curing two different - graded concretes (2 - graded and 3 - graded) at different temperatures (40°C to 80°C). In addition, the study also focused on the change of \[ \text{OH}^- \] concentration in the pore solution and its influence mechanism on ASR expansion, and how these factors change with temperature. Through this study, the author hopes to provide key insights for the development of models for predicting concrete ASR expansion under different environmental conditions and determine the range of curing temperatures suitable for such predictions.