Abstract:Alkali silica reaction (ASR) is an undesirable phenomenon that occurs between alkalis that usually originate from cement and certain types of siliceous aggregates in concrete. The result of this reaction is delayed expansion of hardened concrete in the presence of moisture, which may cause cracking and damage in an existing structure. The present paper investigates the general behavior and shear strength of pretensioned concrete bridge girders affected by ASR. Four identical pretensioned concrete AASHTO Type I girders were fabricated using reactive concrete and subjected to environmental conditioning at a relative humidity of 100% and a temperature of 45 degrees Celsius for up to 296 days to accelerate the development of ASR. During this period, ASR‐induced expansions, changes in surface strains of concrete, transfer lengths, and patterns of damage and cracking were monitored. Each specimen was subjected to shear‐critical loading until failure upon reaching the desired expansion level. The results showed that the existence of prestressing force played a significant role in limiting the ASR‐induced in‐plane expansion and cracking. Progress of ASR caused a reduction in the load corresponding to the first detected flexural crack but an increase by up to 14% in the load corresponding to the first diagonal cracking compared to the control specimen, likely due to the additional prestress caused by restrained ASR‐induced expansions. The ultimate shear strength of ASR‐affected girders was generally within 5% of the control specimens, and all specimens exceeded their nominal shear strengths according to AASHTO LRFD 2020 specifications. Until the unrestrained uniaxial expansion of 0.2%, no significant concerns were identified regarding the shear strength of the ASR‐affected pretensioned concrete specimens.

Effect of ASR expansion on mechanical properties of concrete

Effect of ASR related expansion in the concrete due to alkali concentration and total amount of alkali

Relation of ASR-induced expansion and compressive strength of concrete

Mechanical properties of ASR affected concrete: a critical review

Mechanical Properties of ASR-Affected Concrete Containing Fine or Coarse Reactive Aggregates

Changes in mechanical properties and durability indices of concrete undergoing ASR expansion

Relation between mechanical properties of concrete and alkali-silica reaction (ASR); a review

Time-dependent Effect of Expansion due to Alkali-silica Reaction on Mechanical properties of Concrete

The Effect of Alkali-Silica Reaction (Asr) on the Mechanical Properties of Concretes Containing Trass

Experimental investigation of ASR-affected concrete – The influence of uniaxial loading on the evolution of mechanical properties, expansion and damage indices

Effects of Curing Temperature on Expansion of Concrete Due to ASR

Effect of rock mineralogy on mortar expansion

Effects of Aggregate Shapes and Other Factors on ASR-Induced Anisotropic Expansions in Concrete

INVESTIGATION OF FACTORS INFLUENCING THE EXPANSIVE BEHAVIOUR, COMPRESSIVE STRENGTH AND MODULUS OF RUPTURE OF ALKALI-SILICA REACTIVE CONCRETE USING LABORATORY CONCRETE MIXES

Modelling of Effect of ASR on Concrete Microstructure

Effect of reactive coarse recycled aggregate with different expansion history on alkali silica reactivity and mechanical properties of new concrete

Numerical and experimental study of ASR in concrete at the meso-level

Restraint Effect of Reinforcing Bar on ASR Expansion and Deterioration Characteristic of the Bond Behavior

Environmental impacts on expansion of concrete due to alkali–silica reaction

Effect of alkali silica reaction on pretensioned concrete bridge girders

Determination of ASR in Concrete Using Characterization Methods