Abstract:The alkali–silica reaction (ASR) is a primary cause for premature concrete degradation. An accelerated mortar bar test is often used to access the detrimental phenomena in concrete caused by the ASR of aggregates. However, this test requires a certain environmental conditioning as per ASTM C1260. The objective of this study is to explore the effects of the cement alkali content, exposure solution concentration, temperature, and test duration on mortar bar expansion. Factorial experimental design and analysis was conducted to delineate the effects of the individual factors as well as their interaction. Five different aggregates with various mineralogical properties were used, representing reactive and non-reactive aggregates. Various dosages of cement alkalis (0.40, 0.80, and 1.20 Na2Oe), sodium hydroxide (NaOH) solution concentrations (0.5, 1.0, and 1.5 N), and temperature (40 °C, 80 °C, and 100 °C) were the studied variables. Mortar bar expansion was measured at 3, 7, 14, 21, 28, 56, and 90 days. Mortar bars incorporating Jhelum aggregates incurred expansion of 0.32% at 28 days, proving to be reactive aggregates as per ASTM C1260. Similarly, specimens incorporating Taxila aggregates showed expansion of 0.10% at 28 days, indicating non-reactive nature. It was observed that specimens with Sargodha aggregates showed expansion of 0.27% at 28 days for 0.50 N NaOH solution concentration compared to 0.31% expansion for identical specimens exposed to 1.5 N solution. Moreover, expansion increased with exposure duration for all the tested specimens. Experimental results showed that the cement alkali contents had relatively lesser effect on expansion for 1.0 N NaOH; while, in the case of 0.5 N and 1.5 N NaOH, the cement alkali had a significant effect. It was noted that expansion increased with an increase in the temperature. Jhelum aggregates showed 28-day expansion of 0.290% when exposed to 40 °C, but at a temperature of 100 °C, expansion increased to 0.339%. Factorial analysis revealed that the exposure solution had a major contribution towards the expansion of mortar bar specimens. This study highlights the contribution of various exposure conditions on the ASR expansion, which leads to a decisive role in selecting the aggregate sources for various applications and exposure conditions leading to sustainable construction.

Changes in mechanical properties and durability indices of concrete undergoing ASR expansion

Comparison of Field Observations with Laboratory Test Results on Concretes Undergoing Alkali-Silica Reaction

Relation of ASR-induced expansion and compressive strength of concrete

UNDERSTANDING THE FACTORS AFFECTING EXPANSION DUE TO ALKALI-SILICA REACTION IN CONCRETE

Time-dependent Effect of Expansion due to Alkali-silica Reaction on Mechanical properties of Concrete

Effect of ASR related expansion in the concrete due to alkali concentration and total amount of alkali

Experimental investigation of ASR-affected concrete – The influence of uniaxial loading on the evolution of mechanical properties, expansion and damage indices

Development of Enhanced Test Methods to Evaluate Alkalisilica Reaction in Concrete

INVESTIGATION OF FACTORS INFLUENCING THE EXPANSIVE BEHAVIOUR, COMPRESSIVE STRENGTH AND MODULUS OF RUPTURE OF ALKALI-SILICA REACTIVE CONCRETE USING LABORATORY CONCRETE MIXES

Effect of ASR expansion on mechanical properties of concrete

Effect of Moisture History on ASR Expansion and Microstructural Properties

Alkali–Silica Reactivity Potential of Reactive and Non-Reactive Aggregates under Various Exposure Conditions for Sustainable Construction

Alkali–silica reaction in plain and fibre concretes in field conditions

Long-term ultrasonic monitoring of concrete affected by alkali-silica reaction

Concrete Expansion Induced by Alkali–Silica Reaction in a Small Arch Dam

A study into the alkali-silica reactivity of recycled concrete aggregates and the role of the extent of damage in the source structures: Evaluation, accelerated testing, and preventive measures

Effect of rock mineralogy on mortar expansion

Online Monitoring of the Expansion of Alkali-Silica Reaction Affected Concrete Prisms Implemented to the Accelerated Concrete Prism Test at 60 °C

Failure criteria and microstructure evolution mechanism of the alkali–silica reaction of concrete

Effects of Curing Temperature on Expansion of Concrete Due to ASR

Numerical and experimental study of ASR in concrete at the meso-level