Research on Dynamic Compression Characteristics of Birch Wood Based on SHPB Test
Xu Wei,Hua Jun,Zhang Shaoqun,Chen Guangwei
DOI: https://doi.org/10.11707/j.1001-7488.20150511
2015-01-01
Abstract:Objective]In the refiner grinding dissociation crushing stage,dynamic compression characteristics of wood raw materials were investigated by dynamic compression loading test. [Method]Dynamic compression experiments along radial,tangential and axial loading directions of birch wood (average moisture content and density was 12. 65% and 0. 50 g·cm -3,respectively) were implemented by SHPB experimental device,and the strain rates were approximately 400, 800,1 200 s -1 . The separation behavior during dynamic compression loading processes,dynamic stress-strain curves and the corresponding mechanical properties of wood were obtained in different loading directions and at different strain rates condition. [Result]The comparative analysis results of wood damage patterns indicated that:1) When the strain rate was 400 s -1 ,plastic deformation mainly occurred in specimens,irrespective of radial,tangential or axial loading direction. 2) When the strain rate was 800 s -1 ,radial-loading specimens were separated into several large pieces,and there were some small pieces,like“matchstick”,stripped out from the specimens. Severe plastic deformation was found along the loading direction in tangential-loading specimens. Furthermore,penetrating cracks along the top and bottom surfaces of the specimens were observed in tangential-loading specimens,which were dissociated into three large pieces. As for axial-loading specimens,crushing phenomenon and a large number of penetrating cracks occurred in loading surface,and some small pieces were stripped from the specimens. 3 ) When the strain rate was 1 200 s -1 ,radial-loading specimens were dissociated into a large number of small“matchstick”pieces,and the size was obviously smaller than that at 800 s -1 strain rate. As for the tangential-loading specimens,plastic deformation degree was similar to the situation when strain rate was 800 s -1 . However,the top surfaces of the specimens were separated into several small sheet pieces,and some big cracks throughout the loading direction of specimens can be found. Axial-loading specimens were separated into a number of small stubby shape pieces with wrinkles. The Comparative analysis results of wood stress-strain curve showed that:1) The stress-strain curve can be divided into elastic stage and weak linear strengthening stage by the yield point. 2 ) For radial-loading specimens,when the strain rates were approximately 400,800,1 200 s -1 ,the yield strength and toughness modulus of wood were 4. 56,10. 49,14. 22 MPa and 2. 88,8. 32,20. 70 kJ·cm -3 ,respectively . Furthermore,when the strain rate increased from 400 s -1 to 1 200 s -1 ,the yield stress and toughness modulus increased by 2 . 11 times and 6 . 19 times,respectively. 3) For tangential-loading specimens,when the strain rates were about 400,800,1 200 s -1,the yield strength and toughness modulus of wood were 5. 87,7. 90,9. 65 MPa and 2. 53,7. 41,12. 92 kJ·cm -3 , respectively. Furthermore,when the strain rate increased from 400 s -1 to 1 200 s -1 ,the yield stress and toughness modulus increased by 0. 64 times and 4. 10 times,respectively. 4) For axial-loading specimens,when the strain rates were approximately 400 ,800 ,1 200 s -1 ,the yield strength and toughness modulus of wood were 22 . 90 ,71 . 41 ,96 . 37 MPa and 18. 79,67. 74,114. 32 kJ·cm -3,respectively. Furthermore,when the strain rate increased from 400 s -1 to 1 200 s -1 ,the yield stress and toughness modulus increased by 3. 21 times and 5. 08 times,respectively. [Conclusion]The results showed that dissociation degree of birch increased with the increasing of strain rate. The radial-loading specimens were the most easy to seperate and the axial-loading specimens were the most hard to dissociate. Dynamic compressive yield strength and dynamic compression toughness modulus of Birch exhibited high strain rate sensitivity. Therefore,Birch is a strain rate sensitive material.