Abstract:Tantalum is used as a diffusion barrier and adhesion promoter layer between the dielectric material and copper interconnects. The present study was intended to investigate the effect of oxidizer and solution pH on chemical mechanical planarization of tantalum. High purity Ta disks were used to study the dissolution and oxidation kinetics under static and dynamic conditions using various solutions in acidic and alkaline pH regimes. The electrochemical measurements during dynamic polishing of a Ta disk were carried out using slurries containing silica and alumina particles with hydrogen peroxide at various pH levels. The affected surface layers of the statically etched Ta disk were investigated using X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and secondary ion mass spectrometry (SIMS). Ta metal was observed to oxidize in aqueous solutions at pH 2, 4, and 12 in absence of The oxidation process follows the parabolic kinetic law and oxidation rate was observed to be higher in an alkaline region than in an acidic region. In the presence of however, Ta dissolved in the alkaline region. The dissolution was found to be greater at pH 12 mainly because of enhanced dissociation of in alkaline region. At pH 2, on the contrary, mass gain was observed probably due to an increase in content on the top of Ta oxide formed on the surface as confirmed by XPS and SIMS depth profile studies. XPS study revealed that the oxidation of tantalum takes place at a rapid rate and forms soluble oxotantalate and hydroxotantalate in solution at pH 12 in the presence of hydrogen peroxide. AFM study validates both the XPS and the SIMS results, indicating formation of a thin impervious oxide layer on Ta in a solution at pH 2 with 5% and a porous layer was formed on Ta in solution with 5% at pH 12. Consequently, the dissolution rate in alkaline region was enhanced which was confirmed by dynamic removal rate measurements, electrochemistry, and XPS studies. © 2002 The Electrochemical Society. All rights reserved.

Electrochemical behavior of tantalum in ethylene carbonate and aluminum chloride solvate ionic liquid

Electrodeposition of tantalum and its electrochemical behaviors in molten NaCl-KCl

Electrochemical Behavior of Tantalum in Anhydrous Ethanol

Electrodeposition of Beta-Tantalum in Alkali Metal Halides and Oxohalide Melts

Facile synthesis of nanoscale tantalum powder by electro-deoxidation of Ta2O5

Corrosion Study on Tantalum in Anhydrous Ethanol

Reaction of tantalum oxide with calcium chloride–calcium oxide melts

Kinetics and mechanism of low-temperature aluminothermic reduction of manganese tantalate

Anodic behavior in AlCl3-EMIC ionic liquid of Ti6Al4V alloy and its application for enhancing the adhesion strength of aluminum coatings

Tantalum electrodeposition using a nanoporous anodic alumina template and a nanostructured gold/nickel-chromium glass-ceramic substrate

An in-depth understanding of the solvation effect of methanol on the anisotropy of electrochemical corrosion of Ta

Direct electrochemical reduction of low titanium chlorides into titanium aluminide alloy powders from molten eutectic KCl–LiCl–MgCl2

Method for Recycling Tantalum from Waste Tantalum Capacitors by Chloride Metallurgy

One-step Synthesis of Spherical Al3Ta Alloy Powder by Electrolyzing Solid Ta2O5 in Molten Fluorides

Reduction of Tantalum Pentoxide with Aluminium and Calcium: Thermodynamic Modelling and Scale Skilled Tests

Electrochemical Behaviors of Dy(III) and Its Co-Reduction with Al(III) in Molten LiCl-KCl Salts

Effect of Ph and H[sub 2]o[sub 2] on Ta Chemical Mechanical Planarization

Tuning of Electrical and Optical Properties of Tantalum Doped TiO2 Flims Prepared by Sol-gel Method

Calciothermal reduction of tantalate iron and manganese

Electrochemical Reactions of the Th4+/Th Couple on the Tungsten, Aluminum and Bismuth Electrodes in Chloride Molten Salt

Calciothermic Reduction of Iron and Manganese Tantalates