Abstract:In this article, we report a controllable and reproducible approach to prepare highly ordered 2-D hexagonal mesoporous crystalline TiO2-SiO2 nanocomposites with variable Ti/Si ratios (0 to infinity). XRD, TEM, and N2 sorption techniques have been used to systematically investigate the pore wall structure, and thermal stability functioned with the synthetic conditions. The resultant materials are ultra highly stable (over 900 degrees C), have large uniform pore diameters (approximately 6.8 nm), and have high Brunauer-Emmett-Teller specific surface areas (approximately 290 m2/g). These mesostructured TiO2-SiO2 composites were obtained using titanium isopropoxide (TIPO) and tetraethyl orthosilicate (TEOS) as precursors and triblock copolymer P123 as a template based on the solvent evaporation-induced co-self-assembly process under a large amount of HCl. Our strategy was the synchronous assembly of titanate and silicate oligomers with triblock copolymer P123 by finely tuning the relative humidity of the surrounding atmosphere and evaporation temperature according to the Ti/Si ratio. We added a large amount of acidity to lower condensation and polymerization rates of TIPO and accelerate the rates for TEOS molecules. TEM and XRD measurements clearly show that the titania is made of highly crystalline anatase nanoparticles, which are uniformly embedded in the pore walls to form the "bricked-mortar" frameworks. The amorphous silica acts as a glue linking the TiO2 nanocrystals and improves the thermal stability. As the silica contents increase, the thermal stability of the resulting mesoporous TiO2-SiO2 nanocomposites increases and the size of anatase nanocrystals decreases. Our results show that the unique composite frameworks make the mesostructures overwhelmingly stable; even with high Ti/Si ratios (> or =80/20) the stability of the composites is higher than 900 degrees C. The mesoporous TiO2-SiO2 nanocomposites exhibit excellent photocatalytic activities (which are higher than that for commercial catalyst P25) for the degradation of rhodamine B in aqueous suspension. The excellent photocatalytic activities are ascribed to the bifunctional effect of highly crystallized anatase nanoparticles and high porosity.

Synthesis and Characterization of Titanium Dioxide Nanoparticles for Application in Enhanced Oil Recovery

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Synthesis of Rutile and Anatase TiO2 Nanoparticles from Ti-peroxy Compound Aqueous Solution with Polyols

Synthesis of Titanium Dioxide by Sol-Gel Method and Comparison with Titanium Dioxide Pure

Preparation And Characterization Of Nano-Yb2o3/Tio2 Particles

Physiochemical analysis of titanium dioxide and polyacrylamide nanofluid for enhanced oil recovery at low salinity

Preparation and Characterization of Nanosized Anatase TiO2 Cuboids for Photocatalysis

Preparation of TiO_2 Nanoparticle and Their Photocatalytic Property

Effect of Annealing Temperature on TiO2 Nanostructured Prepared by Sol-Gel Method

Hydrolysis of Titanium Alkoxide in Organic Solvent at High Temperatures: A New Synthetic Method for Nanosized, Thermally Stable Titanium(IV) Oxide

Synthesis and characterization of nanosized anatase TiO2 cuboids

Synthesis of nanometer-sized TiO2 particles by a microemulsion method

Synthesis of titanium dioxide nano-powder via sol–gel method at ambient temperature

Preparation of Anatase-Type TiO_2 Nanoparticals from Ti (SO4)2 Solution under Hydrothermal Conditions and Its Photocatalytic Performance

An amphiphilic nano titanium dioxide based nanofluid: Preparation, dispersion, emulsion, interface properties, wettability and application in enhanced oil recovery

Titanium dioxide (TiO2) Nanoparticles XRD Analyses: An Insight

Preparation and characterization of titanium oxide nanotubes

Controllable and Repeatable Synthesis of Thermally Stable Anatase Nanocrystal-Silica Composites with Highly Ordered Hexagonal Mesostructures.

Nanosized Anatase TiO2 As Precursor for Preparation of Sulfated Titania Catalysts

Synthesis, characterization and catalytic performance of titanium silicalite-1 prepared in micellar media

Preparation and Characterization of Silica-modified Titanium Dioxide Nanoparticles by Co-precipitation Method